AlMn1Mg1 | 3.0526 Material Datasheet

Material Standard Values

Material Models for Simulation

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Material Description

Material Number	Material Number (single)	Standard	Range of Application	Standard Status	Country	Remark
3.0526 (DIN 1725-1 : 1983-02)	3.0526	DIN 1725-1 : 1983-02	DIN 1725-1 : 1983-02 replaced by DIN EN 573-3 : 2003-10 and DIN EN 573-4 : 2004-05	Replaced	Germany	The alloy AlMn1Mg1 has similar properties like AlMn1, however it reaches higher strength (to F 26). It has also relatively high strength in the soft condition, but it is well cold fomrable. The alloy belongs to the nature-hard aluminum materials. A strength increase can be achieved, not by a purposeful heat treatment only by cold forming. It is very well warm and cold transformable and is suitable to the deep-drawing (no lappet formation). The alloy is very corrosion and sea water-steadily. The main field of application, the packing, determines the kind of semi-finished material standardized according to DIN 1788 and DIN 1745 (sheet metal and strip). Application: In the packing (DIN 59606) for cans (dose lower parts, abgestreckte doses), breaking covers and catches of all kinds. In the building industry for roofings (usually profile boards), claddings as well as for roll shutter and roll gates.

Chemical Composition

Cu [%]	Fe [%]	Mg [%]	Mn [%]	Si [%]	Zn [%]	Source	Remark
blur	blur	blur	blur	blur	blur	blur	blur

Mechanical Properties

Semi-finished Product	Condition	Designation of the delivered Condition DIN	Delivery Condition EN	Strength Abbrevation	Nominal Size [mm]	Temperature [°C]	Tensile Strength [MPa]	Yield Strength (0.2% offset) [MPa]	Elongation A10 [%]	Elongation A100 [%]	Elongation A [%]	Hardness HB \| HBW	Source	Remark
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur

Physical Properties

Temperature [°C]	Melting Temperature [°C]	Density [g/cm³]	Young's Modulus [GPa]	Shear Modulus [GPa]	Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1]	Thermal Conductivity [W/(m*K)]	Mean Specific Heat Capacity [kJ/(kg*K)]	Electric Conductivity [MS/m]	Source
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur

Young's Modulus [GPa] vs Temperature [°C]

Exclusive Insight Locked!

This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.

Unlock Now

Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] vs Temperature [°C]

Exclusive Insight Locked!

This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.

Unlock Now

Cross Reference

Material Name	Country	Standard
3004A	Australia	AS 2848.1
3004	Belgium	NBN P21-001
3004	France	NF A 50-451
A-M1G	France	NF A 50-451
3004	France	NF A 50-481
A-M1G	France	NF A 50-481
AlMn1Mg1	USA	AA 3004
AlMn1Mg1	International	ISO 209-1
3004	Italy	UNI 9003/2
6361	Italy	UNI 9003/2
9003/2	Italy	UNI 9003/2
P-AlMn1,2Mg	Italy	UNI 9003/2
A3004P	Japan	JIS H 4000
A3004H	Japan	JIS H 4160
A3004H	Japan	JIS H 4170
AlMn1Mg1	Austria	ÖNORM M 3430
3004	Spain	UNE 38-300
Al-1MnMg	Spain	UNE 38-300
L-3820	Spain	UNE 38-300
3004	Spain	UNE 38-382
Al-1MnMg	Spain	UNE 38-382
L-3820	Spain	UNE 38-382
AlMn1Mg1	Turkey	TS 412
EN AW-Al Mn1Mg1 (EN AW-3004)	Germany	DIN EN 573-3

Producer/Supplier/Trade names

Tradename	Supplier
3540	Novelis AG, Koblenz
3541	Novelis AG, Koblenz
Al-Mn-Mg	Metall Dittrich, Velbert
Alcan WG-4 S	Novelis Deutschland GmbH, Göttingen
Alcan WG-D 4 S	Novelis Deutschland GmbH, Göttingen
AlMn1Mg1	Novelis Deutschland GmbH, Göttingen
AlMn1Mg1	Wieland Prometa GmbH, Düsseldorf

Material Compliance

REACh	RoHS
blur	blur

Formability - Bending - Folding

Condition Number	Strength Abbrevation	Nominal Size [mm]	Rolling Direction	Ductility	Bend Factor	Source
blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur

AlMn1Mg1 (3.0526; DIN 1725-1 : 1983-02)

Linear-elastic

Temperature [°C]	Young's modulus [GPa]	Shear modulus [GPa]	Poisson's ratio
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur

Alternating stress

Temperature [°C]	Stress ratio	Alternating stress [MPa]	Cycles
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Coefficient thermal expansion

Related Temperature [°C]	Temperature [°C]	Coefficient thermal expansion [10^-6*K^-1]
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur

Specific heat

Temperature [°C]	Specific heat [kJ/(kg*K)]
blur	blur

Density

Temperature [°C]	Density [g/cm³]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Thermal conductivity

Temperature [°C]	Thermal conductivity [W/(m*K)]
blur	blur

Classification

WIAM Material	Source description
blur	blur

Designation

Designation	Material number	Source
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur

AlMn1Mg1 (soft annealed (+A); strip; 0.180-0.350mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (soft annealed (+A); strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (1/4 hard; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (1/4 hard, stress-relieved; strip; 0.180-0.300mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (1/4 hard, stress-relieved; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (1/2 hard; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (1/2 hard, stress-relieved; strip; 0.180-0.300mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (1/2 hard, stress-relieved; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (3/4 hard; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (partially annealed; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (hard; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (hard, stress-relieved; strip; 0.180-0.300mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (hard, stress-relieved; strip; 0.350-2.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (spring hard; strip; 0.350-0.450mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (soft annealed (+A))

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Source description
blur	blur

AlMn1Mg1 (G22)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Source description
blur	blur

AlMn1Mg1 (G26)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Source description
blur	blur

AlMn1Mg1 (soft annealed (+A); strip; 0.040-0.069mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (soft annealed (+A); strip; 0.070-0.109mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

AlMn1Mg1 (soft annealed (+A); strip; 0.110-0.179mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur