TiAl6V4 | 3.7165 Material Datasheet

Material Test Series Values

Material Standard Values

Material Models for Simulation

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Material Description

Material Number	Material Number (single)	Standard	Range of Application	Standard Status	Country	Successor	Remark	Application temperature [°C]
3.7165 (DIN 17862 : 1993-02)	3.7165	DIN 17862 : 1993-02	DIN 17862 : 1993-02 replaced by DIN 17862 : 2012-03	Replaced	Germany	TiAl6V4	Chemical composition: DIN 17851 Because of its high quenching distortion during hardening and of the through-hardenability that is limited to approximately 25 mm, the hardenable titanium alloy TiAl6V4 with the material number 3.7165 (see also TiAl6V4, 3.7164, according to the Werkstoff-Leistungsblatt der Deutschen Luftfahrt WL3.7164) is generally used in the annealed condition, except for the manufacturing of small parts, connection components in particular. TiAl6V4 possesses a favourable ratio of strength and weight, a high fracture toughness in the annealed condition and thermal stability in the range from -200 to 400 °C. Corrosion resistance: Good corrosion resistance to strongly oxidizing acids, especially resistant to nitric acid, chromic acid, sulphurous acid, alkali lyes, ammonia, aqueous chlorides, salt brine, sea water, moist chlorine gas, acetic acid, malein acid, liquid hydrogen, limited resistance to sulphuric acid, hydrochloric acid, phosphoric acid, oxalic acid and formic acid. The material is not resistant to fluorine, dry chlorine gas and red fuming nitric acid. There exists resistance to stress cracking corrosion. Processing properties: Formability: limited (cold forming), good (hot forming) Weldability: good (tungsten inert-gas, plasma, electron beam and resistance welding) Application: Fields of application are the engine and airframe construction in the aeroplane industry, measurement devices and valves and fittings, laboratory centrifuges and the automobile sport.	≤ 300

Mechanical Properties

Semi-finished Product	Condition	Condition Number	Strength Abbrevation	Nominal Size [mm]	Temperature [°C]	Specimen Direction	Tensile Strength [MPa]	Yield Strength (0.2% offset) [MPa]	Elongation A [%]	Reduction of Area [%]	Hardness HB \| HBW	Source
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur

Cross Reference

Material Name	Country	Standard
T-A6V	France	AIR 9183
TA28	Great Britain	BS TA 28
TA56	Great Britain	BS TA 56
TA10	Great Britain	BS TA10
TA11	Great Britain	BS TA11
TA12	Great Britain	BS TA12
TA13	Great Britain	BS TA13
VT6s	Russia	GOST 19807
Grade 5	USA	ASTM B 265
Grade 5	USA	ASTM B 337
Grade 5	USA	ASTM B 338
Grade 5	USA	ASTM B 348
Grade 5	USA	ASTM B 363
Grade 5	USA	ASTM B 381
TiAl6V4 (3.7165)	Germany	DIN 17851

Producer/Supplier/Trade names

Tradename	Supplier
Al6V4	Chr. Höver & Sohn GmbH & Co KG, Lindlar
Coralloy Ti-6-4	Chr. Höver & Sohn GmbH & Co. KG, Lindlar
ERGITAN 7165 TV	Stahlwerk Ergste Westig GmbH, Schwerte
LT 31	VDM Metals GmbH, Werdohl
RMI G Al-4V	ZAPP AG, Ratingen
Ti Al6V4	Enpar Sonderwerkstoffe GmbH, Gummersbach
TL64	OTTO FUCHS KG, Meinerzhagen

Material Compliance

REACh	RoHS
blur	blur

Fracture Toughness

Temperature [°C]	Yield Strength [MPa]	Plane-Strain Fracture Toughness KIc [MPa*m^½]	Threshold Stress Intensity Factor at Stress Corrosion Cracking KIscc [MPa*m^½]	Source	Remark
blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur

TiAl6V4 (3.7165; DIN 17862 : 1993-02)

Strain life

Temperature [°C]	Cyclic fatigue strength coefficient [MPa]	Cyclic fatigue strength exponent	Ductility coefficient [Pa]	Ductility exponent	Cyclic strength coefficient [MPa]	Cyclic strain hardening exponent	Young's modulus [GPa]
blur	blur	blur	blur	blur	blur	blur	blur

Linear-elastic

Temperature [°C]	Young's modulus [GPa]	Poisson's ratio
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

WIAM Material	Source description
blur	blur

Designation

Designation	Material number	Source
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur

TiAl6V4 (tension/compression; fracture)

Alternating stress

Temperature [°C]	Stress ratio	Alternating stress [MPa]	Cycles
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur

Classification

Load type	Failure criteria	Source description
blur	blur	blur

TiAl6V4 (6mm; flaw)

Strain life

Temperature [°C]	Cyclic fatigue strength coefficient [MPa]	Cyclic fatigue strength exponent	Ductility coefficient [Pa]	Ductility exponent	Cyclic strength coefficient [MPa]	Cyclic strain hardening exponent	Young's modulus [GPa]
blur	blur	blur	blur	blur	blur	blur	blur

Classification

Dimension [mm]	Failure criteria	Source description
blur	blur	blur

TiAl6V4 (precipitation hardened (+P); 6.35mm; fracture)

Strain life

Temperature [°C]	Cyclic fatigue strength coefficient [MPa]	Cyclic fatigue strength exponent	Ductility coefficient [Pa]	Ductility exponent	Cyclic strength coefficient [MPa]	Cyclic strain hardening exponent	Young's modulus [GPa]
blur	blur	blur	blur	blur	blur	blur	blur

Classification

Treatment	Dimension [mm]	Failure criteria	Source description
blur	blur	blur	blur

TiAl6V4 (precipitation hardened (+P); load drop)

Strain life

Temperature [°C]	Cyclic fatigue strength coefficient [MPa]	Cyclic fatigue strength exponent	Ductility coefficient [Pa]	Ductility exponent	Cyclic strength coefficient [MPa]	Cyclic strain hardening exponent	Young's modulus [GPa]
blur	blur	blur	blur	blur	blur	blur	blur

Classification

Treatment	Failure criteria	Source description
blur	blur	blur

TiAl6V4 (soft annealed (+A); rod; 6.000-80.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

TiAl6V4 (soft annealed (+A); rod; 80.000-150.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

TiAl6V4 (artificially aged; rod; 6.000-25.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

TiAl6V4 (soft annealed (+A))

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Source description
blur	blur

TiAl6V4 (artificially aged)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur
blur	blur

Classification

Treatment	Source description
blur	blur

TiAl6V4 | 3.7165 Material Datasheet

Material Test Series Values

Material Standard Values

Material Models for Simulation

Material Description

Mechanical Properties

Cross Reference

Producer/Supplier/Trade names

Material Compliance

Fracture Toughness

TiAl6V4 (3.7165; DIN 17862 : 1993-02)

Strain life

Linear-elastic

Yield strength

Tensile strength

Classification

Designation

TiAl6V4 (tension/compression; fracture)

Alternating stress

Classification

TiAl6V4 (6mm; flaw)

Strain life

Classification

TiAl6V4 (precipitation hardened (+P); 6.35mm; fracture)

Strain life

Classification

TiAl6V4 (precipitation hardened (+P); load drop)

Strain life

Classification

TiAl6V4 (soft annealed (+A); rod; 6.000-80.000mm)

Yield strength

Tensile strength

Classification

TiAl6V4 (soft annealed (+A); rod; 80.000-150.000mm)

Yield strength

Tensile strength

Classification

TiAl6V4 (artificially aged; rod; 6.000-25.000mm)

Yield strength

Tensile strength

Classification

TiAl6V4 (soft annealed (+A))

Yield strength

Tensile strength

Classification

TiAl6V4 (artificially aged)

Tensile strength

Classification

Similar Materials