EN AW-Al Mg2Mn0,3 | EN AW-5251 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Predecessor | Successor | Remark |
|---|---|---|---|---|---|---|---|---|
| EN AW-5251 (DIN EN 573-3 : 2009-08) | EN AW-5251 | DIN EN 573-3 : 2009-08 | DIN EN 573-3 : 2009-08 replaced by DIN EN 573-3 : 2013-12 | Replaced | Germany | EN AW-Al Mg2Mn0,3 | EN AW-Al Mg2Mn0,3 | Material EN AW-Al Mg2 is produced for sheet metals, strip and plates, for HF-welded tubes, for wire and prewire for mechanical applications, for extruded and drawn components. The material is food-safe and is used for prematerial for cans, caps and stoppers. To the comparable mark AlMg2Mn0,3, material No. 3.3525 acc. to DIN 1725-1 : 1983-02 applies: The alloy AlMg2Mn0,3 is similar to alloy AlMg1,8. Mn-addition causes strength increase for extrusion products and hightened high-temperature strength of the material. It has a high resistance to corrosion, seawater and salted atmosphere. Strength increases and cold workability decreases according to the Mg-content. It is naturally hard, i.e. a strength increase can only be achieved by cold forming, not by controlled heat treatment. Machinability and weldability are enhanced by increasing Mg-content. Application: for metal goods (incl. harness), in food industry (incl. commercial devices). For transport containers, in packaging industry as tins as well as for signs (e.g traffic signs). |
Chemical Composition
| Cr [%] | Cu [%] | Fe [%] | Mg [%] | Mn [%] | Si [%] | Ti [%] | Zn [%] | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Designation of the delivered Condition DIN | Nominal Size [mm] | Temperature [°C] | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A100 [%] | Elongation A [%] | Elongation A50 [%] | Hardness HB | HBW | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Physical Properties
| Temperature [°C] | Melting Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Shear Modulus [GPa] | Poisson's Ratio | Thermal Conductivity [W/(m*K)] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | Electric Conductivity [MS/m] | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Young's Modulus [GPa] vs Temperature [°C]
Exclusive Insight Locked!
This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.
Unlock NowCross Reference
| Material Name | Country | Standard |
|---|---|---|
| 5251 | Australia | AS 2848.1 |
| 5251 | China | GB/T 3880 |
| 1520 | Russia | GOST 4784 |
| AMg2 | Russia | GOST 4784 |
| 5251 | USA | International Registration Record (AA) |
| AlMg2 | International | ISO 209-1 |
| AlMg2Mn0,3 | Turkey | TS 412 |
| A95251 | USA | UNS |
| AlMg2Mn0,3 (3.3525) | Germany | DIN 1725-1 |
| AlMg2Mn0,3 (3.3525) | Germany | DIN 1745-1 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| AlMg2 | Swiss Steel International GmbH, Düsseldorf |
| AlMg2 | Voß Edelstahlhandel GmbH & Co.KG, Neu Wulmstorf |
| EN AW-AlMg2 | Martinrea Honsel Germany GmbH, Meschede |
| EN AW-AlMg2 | TRIMET ALUMINIUM AG, Essen |
| AlMg2 | Imet Industriemetall Handelsgesellschaft mbH, Hamburg |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
FKM Guideline Fatigue Strength
| Semi-finished Product | Condition | Nominal Size [mm] | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | Elongation A50 [%] | Fatigue Limit under rev. Tension-Compression Stresses [MPa] | Fatigue Strength under pulsating Tensile Stresses [MPa] | Bending Fatigue Strength [MPa] | Shear Fatigue Strength [MPa] | Torsion Fatigue Strength [MPa] | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Formability - Bending - Folding
| Semi-finished Product | Condition | Nominal Size [mm] | Bend Factor (90°) | Bend Factor (180°) | Source |
|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (EN AW-5251; DIN EN 573-3 : 2009-08)
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Alternating stress [MPa] | Cycles |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Source description |
|---|---|
| blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 0.000-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 1.500-0.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H44 (strain-hardened and painted or lacquered - 1/2 hard); strip; 0.000-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H44 (strain-hardened and painted or lacquered - 1/2 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H44 (strain-hardened and painted or lacquered - 1/2 hard); strip; 1.500-0.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H46 (strain-hardened and painted or lacquered - 3/4 hard); strip; 0.000-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H46 (strain-hardened and painted or lacquered - 3/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H46 (strain-hardened and painted or lacquered - 3/4 hard); strip; 1.500-0.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H48 (strain-hardened and painted or lacquered - 4/4 hard); strip; 0.000-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H48 (strain-hardened and painted or lacquered - 4/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H48 (strain-hardened and painted or lacquered - 4/4 hard); strip; 1.500-0.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H16 (strain-hardened - 3/4 hard); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H26 (strain-hardened and partially annealed - 3/4 hard); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); strip; 12.500-50.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); strip; 12.500-50.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); strip; 12.500-25.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H16 (strain-hardened - 3/4 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H16 (strain-hardened - 3/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H16 (strain-hardened - 3/4 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H16 (strain-hardened - 3/4 hard); strip; 3.000-4.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H18 (strain-hardened - 4/4 hard (fully hardened)); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H18 (strain-hardened - 4/4 hard (fully hardened)); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H18 (strain-hardened - 4/4 hard (fully hardened)); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); strip; 12.500-25.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H32 (strain-hardened and stabilized -1/4 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H32 (strain-hardened and stabilized -1/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H32 (strain-hardened and stabilized -1/4 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H32 (strain-hardened and stabilized -1/4 hard); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H32 (strain-hardened and stabilized -1/4 hard); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H32 (strain-hardened and stabilized -1/4 hard); strip; 12.500-25.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); strip; 3.000-6.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); strip; 6.000-12.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H26 (strain-hardened and partially annealed - 3/4 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H26 (strain-hardened and partially annealed - 3/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H26 (strain-hardened and partially annealed - 3/4 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H26 (strain-hardened and partially annealed - 3/4 hard); strip; 3.000-4.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H36 (strain-hardened and stabilized - 3/4 hard); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H36 (strain-hardened and stabilized - 3/4 hard); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H36 (strain-hardened and stabilized - 3/4 hard); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H36 (strain-hardened and stabilized - 3/4 hard); strip; 3.000-4.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H28 (strain-hardened and partially annealed - 4/4 hard (fully hardened)); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H28 (strain-hardened and partially annealed - 4/4 hard (fully hardened)); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H28 (strain-hardened and partially annealed - 4/4 hard (fully hardened)); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H38 (strain-hardened and stabilized - 4/4 hard (fully hardened)); strip; 0.200-0.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H38 (strain-hardened and stabilized - 4/4 hard (fully hardened)); strip; 0.500-1.500mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H38 (strain-hardened and stabilized - 4/4 hard (fully hardened)); strip; 1.500-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); rod; 0.000-80.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); rod; 0.000-60.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); rod; 0.000-80.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); rod; 0.000-60.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); rod; 0.000-30.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); rod; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); rod; 0.000-30.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); rod; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); rod; 0.000-30.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); rod; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H18 (strain-hardened - 4/4 hard (fully hardened)); rod; 0.000-20.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H18 (strain-hardened - 4/4 hard (fully hardened)); rod; 0.000-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H28 (strain-hardened and partially annealed - 4/4 hard (fully hardened)); rod; 0.000-20.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H28 (strain-hardened and partially annealed - 4/4 hard (fully hardened)); rod; 0.000-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H38 (strain-hardened and stabilized - 4/4 hard (fully hardened)); rod; 0.000-20.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H38 (strain-hardened and stabilized - 4/4 hard (fully hardened)); rod; 0.000-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); tube; 0.000-20.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); tube; 0.000-20.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H12 (strain-hardened - 1/4 hard); tube; 0.000-10.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H22 (strain-hardened and partially annealed - 1/4 hard); tube; 0.000-10.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H32 (strain-hardened and stabilized -1/4 hard); tube; 0.000-10.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); tube; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H24 (strain-hardened and partially annealed - 1/2 hard); tube; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H34 (strain-hardened and stabilized - 1/2 hard); tube; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H16 (strain-hardened - 3/4 hard); tube; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H26 (strain-hardened and partially annealed - 3/4 hard); tube; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H36 (strain-hardened and stabilized - 3/4 hard); tube; 0.000-5.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H18 (strain-hardened - 4/4 hard (fully hardened)); tube; 0.000-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H28 (strain-hardened and partially annealed - 4/4 hard (fully hardened)); tube; 0.000-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H38 (strain-hardened and stabilized - 4/4 hard (fully hardened)); tube; 0.000-3.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (production state; rod)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H112 (slightly strain-hardened from working at an elevated temperature or from a limited amount of cold work); rod)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); rod)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); rod)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (production state; tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H112 (slightly strain-hardened from working at an elevated temperature or from a limited amount of cold work); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H111 (annealed and slightly strain-hardened (less than H11) during subsequent operations such as stretching or levelling); tube)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (production state; section)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H112 (slightly strain-hardened from working at an elevated temperature or from a limited amount of cold work); section)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Source description |
|---|---|---|
| blur | blur | blur |
EN AW-Al Mg2Mn0,3 (soft annealed (+A); wire; 0.000-20.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H14 (strain-hardened - 1/2 hard); wire; 0.000-18.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (H18 (strain-hardened - 4/4 hard (fully hardened)); wire; 0.000-10.000mm)
Yield strength
| Temperature [°C] | 0.2% Proof strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EN AW-Al Mg2Mn0,3 (production state; strip; 2.500-80.000mm)
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |