EStE 355 | 1.1106 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Successor | Remark | Application temperature [°C] |
|---|---|---|---|---|---|---|---|---|
| 1.1106 (DIN 17102 : 1983-10) | 1.1106 | DIN 17102 : 1983-10 | DIN 17102 : 1983-10 replaced by DIN EN 10025-1/-3 : 2005-02, DIN EN 10028-1/-3 : 2003-09 | Replaced | Germany | P355NL2 | The fine grained steel EStE 355 is used for welded constructions of different kind like pressure vessels, stationary or mobile storage tanks, high pressure lines, bridge and support constructions etc. The application temperature of the tough at subzero temperatures grade amounts to -60 °C. | ≥ -60 |
Chemical Composition
| Al [%] | C [%] | Cr [%] | Cu [%] | Mn [%] | Mo [%] | N [%] | Nb [%] | Ni [%] | P [%] | S [%] | Si [%] | V [%] | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength [MPa] | Elongation A [%] | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Differential Coefficient of Thermal Expansion [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Thermal Diffusivity [10^-6 m²/s] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | True Specific Heat Capacity [kJ/(kg*K)] | Source |
|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Young's Modulus [GPa] vs Temperature [°C]
Exclusive Insight Locked!
This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.
Unlock NowMean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] vs Temperature [°C]
Exclusive Insight Locked!
This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.
Unlock NowDifferential Coefficient of Thermal Expansion [10^-6*K^-1] vs Temperature [°C]
Exclusive Insight Locked!
This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.
Unlock NowToughness Data (Impact)
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Shape | Specimen Direction | Notch Impact Energy [J] | Source |
|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | Source | Remark |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| A 52 AP | France | NF A 36-205 |
| 50 C | Great Britain | BS 4360 |
| Grade C | USA | ASTM A 500 |
| P355NL2 | Germany | DIN EN 10028-3 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| Aldur E 36 E | voestalpine AG, Linz |
| Dillinal 50/36 E | AG der Dillinger Hüttenwerke, Dillingen |
| DIRO P355NL2 | DIROSTAHL, Remscheid |
| P355NL2 | Hoesch Hohenlimburg GmbH, Hagen |
| P355NL2 | ThyssenKrupp Steel Europe AG, Duisburg |
| P355NL2 | Schmiedewerke Gröditz GmbH, Gröditz |
| SB 36 FTT | Salzgitter Flachstahl GmbH, Salzgitter |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
FKM Guideline Fatigue Strength
| Semi-finished Product | Condition | Nominal Size [mm] | Tensile Strength [MPa] | Yield Strength [MPa] | Fatigue Limit under rev. Tension-Compression Stresses [MPa] | Fatigue Strength under pulsating Tensile Stresses [MPa] | Bending Fatigue Strength [MPa] | Shear Fatigue Strength [MPa] | Torsion Fatigue Strength [MPa] | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
EStE 355 (1.1106; DIN 17102 : 1983-10)
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Poisson's ratio |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Alternating stress [MPa] | Cycles |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Coefficient thermal expansion
| Related Temperature [°C] | Temperature [°C] | Coefficient thermal expansion [10^-6*K^-1] |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Source description |
|---|---|
| blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
EStE 355 (tension/compression; flaw)
Alternating stress
| Temperature [°C] | Stress ratio | Alternating stress [MPa] | Cycles |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Classification
| Load type | Failure criteria | Source description |
|---|---|---|
| blur | blur | blur |
EStE 355 (tension/compression; fracture)
Alternating stress
| Temperature [°C] | Stress ratio | Alternating stress [MPa] | Cycles |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Classification
| Load type | Failure criteria | Source description |
|---|---|---|
| blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); tube; 0.000-12.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (cold worked, welded and normalized; section; 0.000-12.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (hot worked, normalized; section; 0.000-12.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); Large I , H, U shaped sections; 0.000-35.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); tube; 12.000-20.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (cold worked, welded and normalized; section; 12.000-20.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (hot worked, normalized; section; 12.000-20.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); tube; 20.000-40.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (cold worked, welded and normalized; section; 20.000-40.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (hot worked, normalized; section; 20.000-40.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); Large I , H, U shaped sections; 35.000-50.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); tube; 40.000-50.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (cold worked, welded and normalized; section; 40.000-50.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (hot worked, normalized; section; 40.000-50.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); tube; 50.000-65.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (cold worked, welded and normalized; section; 50.000-65.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (hot worked, normalized; section; 50.000-65.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); Large I , H, U shaped sections; 50.000-70.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); Large I , H, U shaped sections; 70.000-85.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); Large I , H, U shaped sections; 85.000-100.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); Large I , H, U shaped sections; 100.000-125.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); Large I , H, U shaped sections; 125.000-150.000mm)
Yield strength
| Temperature [°C] | Yield strength [MPa] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |
EStE 355 (normalized or normalized formed (+N); bar; 40.000mm)
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| Treatment | Semi-finished product | Dimension [mm] | Source description |
|---|---|---|---|
| blur | blur | blur | blur |