CuZn39Pb3 | 2.0401 Material Datasheet

Material Test Series Values

Material Standard Values

Material Models for Simulation

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Material Description

Material Number	Material Number (single)	Standard	Standard Status	Country	Remark
2.0401 (DIN 17660 : 1983-12)	2.0401	DIN 17660 : 1983-12	Withdrawn without replacement	Germany	CuZn39Pb3 is a non-hardenable wrought alloy. High hardness and strength can only be reached by cold forming. Strength values between F37 and F51. Heat and electrical conductivity lower compared to lead-free brass of the same Zn content. Addition of Pb improve the machinability. Corrosion resistance to water, different salt solutions and organic liquids is lower compared to lead-free alloys with the same content of Zn. (CuZn40) Processing properties: Hot forming: very well Cold forming: poorly Machinability: very well Brazing: medium Soldering: very well TIG-welding: poorly Polishability: very well Application: main grade for machining, turning parts for fine mechanics, clocks, electrical engineering

Chemical Composition

Al [%]	Cu [%]	Fe [%]	Ni [%]	Pb [%]	Sn [%]	Source	Remark
blur	blur	blur	blur	blur	blur	blur	blur

Mechanical Properties

Semi-finished Product	Condition	Condition Number	Strength Abbrevation	Nominal Size [mm]	Temperature [°C]	Tensile Strength [MPa]	Yield Strength (0.2% offset) [MPa]	Elongation A100 [%]	Elongation A [%]	Hardness HB \| HBW	Source	Remark
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur

Physical Properties

Temperature [°C]	Melting Temperature [°C]	Density [g/cm³]	Young's Modulus [GPa]	Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1]	Thermal Conductivity [W/(m*K)]	Specific Electrical Resistance [µΩm]	Mean Specific Heat Capacity [kJ/(kg*K)]	Electric Conductivity [MS/m]	Source	Remark
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	blur

Young's Modulus [GPa] vs Temperature [°C]

Exclusive Insight Locked!

This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.

Unlock Now

Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] vs Temperature [°C]

Exclusive Insight Locked!

This premium diagram is currently blurred. Gain full access to detailed insights and stay ahead with exclusive content.

Unlock Now

Cross Reference

Material Name	Country	Standard	Source
CuZn40Pb3	France	NF A51-105
CZ 121	Great Britain	BS 2870
CZ 121	Great Britain	BS 2871
CZ 121	Great Britain	BS 2872
CZ 121	Great Britain	BS 2873
CZ 121	Great Britain	BS 2874
CZ 121	Great Britain	BS 2875
LS59-3	Russia	GOST 15527-70
CuZn39Pb3	International	ISO 426/2-83
MO58A	Poland	PN-77/H-87025
CuZn39Pb3	Romania	STAS 95-80
CuZn39Pb3	Hungary	MSZ 770/1-77
C38500	USA	ASTM B 455
CuZn39Pb3 (CW614N)	Germany	DIN EN 12165
CuZn39Pb3 (CW614N)	Germany	DIN EN 12166
CuZn39Pb3 (CW614N)	Germany	DIN EN 12167
CuZn39Pb3 (CW614N)	Germany	DIN EN 12168
CuZn39Pb3 (CW614N)	Germany	DIN EN 12420
CuZn39Pb3 (CW614N)	Germany	DIN EN 12164
CuZn39Pb3 (CW614N)	Germany	DIN EN 12449
Ms58	Germany		DIN 1755-1

Producer/Supplier/Trade names

Tradename	Supplier
002	Diehl Metall Stiftung & Co. KG, Röthenbach
2158	OTTO FUCHS KG, Meinerzhagen
2359	OTTO FUCHS KG, Meinerzhagen
252	William Prym Holding GmbH, Stolberg
253	William Prym Holding GmbH, Stolberg
2558	OTTO FUCHS KG, Meinerzhagen
CuZn39Pb3	ThyssenKrupp Schulte GmbH, Essen
CuZn39Pb3	OTTO FUCHS KG, Meinerzhagen
CuZn39Pb3	Peterseim GmbH & Co. KG, Olpe
CuZn39Pb3	Schreier Metall GmbH, Erkrath
CuZn39Pb3	Wieland Prometa GmbH, Düsseldorf
CuZn39Pb3	Eugen Geyer GmbH, Königsbach-Stein
CuZn39Pb3	Metall Dittrich, Velbert
CuZn39Pb3	DELWO Metallhandel GmbH, Neunkirchen
CuZn39Pb3	Manfred J.C. Niemann, Bremen
CuZn39Pb3,5	OTTO FUCHS KG, Meinerzhagen
Ms 58 A	Swissmetal Lüdenscheid GmbH, Lüdenscheid
Ms 58 D	Swissmetal Lüdenscheid GmbH, Lüdenscheid
Ms58	F. Hackländer GmbH, Kassel
Ms58F	KME Brass Germany GmbH, Berlin
Ms58H	KME Brass Germany GmbH, Berlin
Ms58M	KME Brass Germany GmbH, Berlin
Ms58P	KME Brass Germany GmbH, Berlin
Ms58S	KME Brass Germany GmbH, Berlin
Z32	Wieland-Werke AG, Ulm
Z33	Wieland-Werke AG, Ulm

Material Compliance

REACh	RoHS
blur	blur

CuZn39Pb3 (2.0401; DIN 17660 : 1983-12)

Linear-elastic

Temperature [°C]	Young's modulus [GPa]	Poisson's ratio
blur	blur	blur
blur	blur	blur

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Electrical resistivity

Temperature [°C]	Specific electrical resistance [µΩm]
blur	blur
blur	blur

Coefficient thermal expansion

Related Temperature [°C]	Temperature [°C]	Coefficient thermal expansion [10^-6*K^-1]
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur

Specific heat

Temperature [°C]	Specific heat [kJ/(kg*K)]
blur	blur

Density

Temperature [°C]	Density [g/cm³]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur

Thermal conductivity

Temperature [°C]	Thermal conductivity [W/(m*K)]
blur	blur

Classification

WIAM Material	Source description
blur	blur

Designation

Designation	Material number	Source
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur

CuZn39Pb3 (soft annealed (+A); tube; 0.000-10.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (1/2 hard; tube; 0.000-10.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (hard; tube; 0.000-5.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (soft annealed (+A); rod; 10.000-0.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (soft annealed (+A); rod; 8.000-0.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (soft annealed (+A); rod; 6.000-0.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (1/2 hard; rod; 0.000-40.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (1/2 hard; rod; 0.000-35.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (1/2 hard; rod; 0.000-6.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (hard; rod; 0.000-14.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (hard; rod; 0.000-10.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (hard; rod; 0.000-4.000mm)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (forged; drop forging)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Source description
blur	blur	blur

CuZn39Pb3 (soft annealed (+A); section)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur

Classification

Treatment	Semi-finished product	Source description
blur	blur	blur

CuZn39Pb3 (1/2 hard; section)

Yield strength

Temperature [°C]	0.2% Proof strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Source description
blur	blur	blur

CuZn39Pb3 (1/2 hard; wire; 8.000-12.000mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (1/2 hard; wire; 3.000-8.000mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (hard; wire; 3.000-8.000mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (hard; wire; 1.500-3.000mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (hard; wire; 0.500-1.500mm)

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

Treatment	Semi-finished product	Dimension [mm]	Source description
blur	blur	blur	blur

CuZn39Pb3 (soft annealed (+A))

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur
blur	blur
blur	blur

Classification

Treatment	Source description
blur	blur