X2CrNi19-11 | 1.4306 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Scope | Standard Status | Country | Predecessor | Successor | VDA 231-106 classification | |
|---|---|---|---|---|---|---|---|---|---|
| 1.4306 (DIN EN 10216-5 : 2004-11) | 1.4306 | DIN EN 10216-5 : 2004-11 | DIN EN 10216-5 : 2004-11 replaced by DIN EN 10216-5 : 2014-03 | Replaced | Germany | X2CrNi19-11 | X2CrNi19-11 | 1.1 | 1) |
| 1) Remark: Material X2CrNi19-11a modifikation of 1.4301 is comparable to X 2CrNi 19 11 acc. to DIN 17440 : 1985-07 (invalid). The steel shows owing to the lowered C-content resistance to intercrystalline corrosion both in delivery and sensitized condition. Application in chemical apparatus engineering and in pharmaceutical industry, especially when high wall thickness and simultaneous suitability for mirror finishing are requested in atomic reactor technology, for parts in food industry which are exposed to organic or fruit acids, in oil, soap and synthetic fibre industry. Generally resistant up to pH-value 4,5 in aggressive agents. |
Chemical Composition
| C [%] | Cr [%] | Mn [%] | N [%] | Ni [%] | P [%] | S [%] | Si [%] | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||
| 2) Remark: blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Yield Strength (1.0% offset) [MPa] | Elongation A [%] | |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur | |||||||||
| 2) Remark: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| 00Cr19Ni10 | China | GB/T 14976 |
| S30403 | China | GB/T 13296 |
| 20Cr18Ni2 | India | IS 11714-4 |
| SUS304LTB | Japan | JIS G 3463 |
| STS304LTB | South Korea | KS D 3577 |
| S30403 | USA | UNS |
| 304L | USA | ASTM A 213 |
| 304L | USA | ASME SA 213 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| DMV 304 L | Salzgitter Mannesmann Stainless Tubes GmbH, Mülheim an der Ruhr |
| VALIMA 304 L | Salzgitter Mannesmann Stainless Tubes GmbH, Mülheim an der Ruhr |
| 3R12 | SANDVIK Materials TEchnology Deutschland GmbH, Düsseldorf |
| A600 | Schoeller-Bleckmann Edelstahlrohr GmbH, Ternitz |
| 4306 | Riba Edelstahl Handelsgesellschaft mbH, Hamburg |
| 1.4306 | TPS-Technitube Röhrenwerke GmbH, Daun |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |