TStE 460 | 1.8915 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Name | Material Number (single) | Standard | Scope | Standard Status | Country | Successor | VDA 231-106 classification | Application temperature [°C] | |
|---|---|---|---|---|---|---|---|---|---|---|
| 1.8915 (DIN 17102 : 1983-10) | TStE 460 | 1.8915 | DIN 17102 : 1983-10 | DIN 17102 : 1983-10 replaced by DIN EN 10025-1/-3 : 2005-02, DIN EN 10028-1/-3 : 2003-09 | Replaced | Germany | P460NL1 | 1.1.1 | ≥ -50 | 1) |
| 1) Remark: The fine grained steel TStE 460 is used for welded constructions of different kind like pressure vessels, stationary or mobile storage tanks, high pressure lines, bridge and support constructions etc. The application temperature of the tough at subzero temperatures grade amounts to -50 °C. |
Chemical Composition
| Al [%] | C [%] | Cr [%] | Cu [%] | Mn [%] | Mo [%] | N [%] | Nb [%] | Ni [%] | P [%] | S [%] | Si [%] | V [%] | Remainder | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||||||||
| 2) Remark: blur |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength [MPa] | Elongation A [%] | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 7)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 5)6) |
| 1) Source: blur | ||||||||
| 2) Remark: blur | ||||||||
| 3) Source: blur | ||||||||
| 4) Remark: blur | ||||||||
| 5) Source: blur | ||||||||
| 6) Remark: blur | ||||||||
| 7) Source: blur | ||||||||
| 8) Remark: blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Differential Coefficient of Thermal Expansion [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Thermal Diffusivity [10^-6 m²/s] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | True Specific Heat Capacity [kJ/(kg*K)] | |
|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Toughness Data (Impact)
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Shape | Specimen Direction | Notch Impact Energy [J] | |
|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | 4) |
| 1) Source: blur | |||||||
| 2) Source: blur | |||||||
| 3) Source: blur | |||||||
| 4) Source: blur |
FKM Guideline Fatigue Strength
| Semi-finished Product | Condition | Nominal Size [mm] | Tensile Strength [MPa] | Yield Strength [MPa] | Fatigue Limit under rev. Tension-Compression Stresses [MPa] | Fatigue Strength under pulsating Tensile Stresses [MPa] | Bending Fatigue Strength [MPa] | Shear Fatigue Strength [MPa] | Torsion Fatigue Strength [MPa] | |
|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||||
| 2) Remark: blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | |
|---|---|---|
| blur | blur | 1)2) |
| blur | blur | 2)3) |
| blur | blur | 2)3) |
| 1) Source: blur | ||
| 2) Remark: blur | ||
| 3) Source: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| 55 F | Great Britain | BS 4360 |
| Y 65 | USA | ASTM A 381 |
| P460NL1 | Germany | DIN EN 10028-3 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| Aldur ENiVT | voestalpine AG, Linz |
| Dillinal 58/47 AT | AG der Dillinger Hüttenwerke, Dillingen |
| DIRO-P460NL1 | DIROSTAHL, Remscheid |
| FG 47 T (CT) | Vallourec Deutschland GmbH, Mülheim |
| P460NL1 | Hoesch Hohenlimburg GmbH, Hagen |
| P460NL1 | ThyssenKrupp Steel Europe AG, Duisburg |
| P460NL1 | Hayes-Lemmerz-Werke GmbH, Königswinter |
| P460NL1 | Schmiedewerke Gröditz GmbH, Gröditz |
| SB 47 FAK | Salzgitter Flachstahl GmbH, Salzgitter |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Coefficient thermal expansion
| Related Temperature [°C] | Temperature [°C] | Coefficient thermal expansion [10^-6*K^-1] |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |