S355J2G4C | 1.0579 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Successor | Application temperature [°C] | |
|---|---|---|---|---|---|---|---|---|
| 1.0579 (DIN EN 10025 : 1994-03) | 1.0579 | DIN EN 10025 : 1994-03 | DIN EN 10025 : 1994-03 replaced by DIN EN 10025-1 : 2005-02 and DIN EN 10025-2 : 2005-04 | Replaced | Germany | S355J2C | ≥ -20 | 1) |
| 1) Remark: S355J2G4C is used for folding, section cold forming and cold drawing grade. The high-tensile fine grained steel is applicable for welding constructions of dynamic load up to -20 °C. Compared to S235J2G4C is achievable a considerable saving of material due to the by 120 MPa higher yield point. The steel shows a by 15% higher resistance to mineral wear due to sliding action in comparison to S235J2G4. Mechanical properties have to comply with EURONORM 164 by arrangement. Max. product thickness amounts 20 mm for folding and 8 mm for cold roll forming grades. |
Chemical Composition
| C [%] | Mn [%] | P [%] | S [%] | Si [%] | |
|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | |||||
| 2) Remark: blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength [MPa] | Elongation A [%] | Elongation A80 [%] | |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| 1) Source: blur | |||||||||
| 2) Remark: blur | |||||||||
| 3) Remark: blur | |||||||||
| 4) Remark: blur |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| S355J2G4C | ArcelorMittal Commercial Germany, Cologne |
| S355J2G4C | Salzgitter Flachstahl GmbH, Salzgitter |
| S355J2G4C | ThyssenKrupp Steel Europe AG, Duisburg |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Formability - Bending - Folding
| Condition | Nominal Size [mm] | Radius of Bend [mm] | Rolling Direction | |
|---|---|---|---|---|
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | 1)3) |
| 1) Source: blur | ||||
| 2) Remark: blur | ||||
| 3) Remark: blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |