P275NH | 1.0487 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Scope | Standard Status | Country | Predecessor | Successor | Application temperature [°C] | VDA 231-106 classification | |
|---|---|---|---|---|---|---|---|---|---|---|
| 1.0487 (DIN EN 10028-3 : 2003-09) | 1.0487 | DIN EN 10028-3 : 2003-09 | DIN EN 10028-3 : 2003-09 replaced by DIN EN 10028-3 : 2009-09 | Replaced | Germany | WStE 285 | P275NH | ≤ 400 | 1.1 | 1) |
| 1) Remark: Heat-resistant weldable fine grain steel (unalloyed quality steel) for application in steam boiler and pressure vessel construction. Max. application temperature: approx. 400 °C. |
Chemical Composition
| Al [%] | C [%] | Cr [%] | Cu [%] | Mn [%] | Mo [%] | N [%] | Nb [%] | Ni [%] | P [%] | S [%] | Si [%] | Ti [%] | V [%] | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Tensile Strength [MPa] | Yield Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | 4)6) |
| 1) Source: blur | ||||||||
| 2) Remark: blur | ||||||||
| 3) Remark: blur | ||||||||
| 4) Source: blur | ||||||||
| 5) Remark: blur | ||||||||
| 6) Remark: blur |
Toughness Data (Impact)
| Condition | Nominal Size [mm] | Temperature [°C] | Specimen Shape | Specimen Direction | Notch Impact Energy [J] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | 3)4) |
| 1) Source: blur | ||||||
| 2) Remark: blur | ||||||
| 3) Source: blur | ||||||
| 4) Remark: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| P275NH | Europe | EN 10028-3 |
| A 42 FP | France | NF A 36-205 |
| 43 C | Great Britain | BS 4360 |
| Grade A | USA | ASTM A 662 |
| WStE 285 | Germany | DIN 17102 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| Aldur E 29 W | voestalpine AG, Linz |
| BGH 0487 | BGH Edelstahl Siegen GmbH |
| Dillinal 40/29 W | AG der Dillinger Hüttenwerke, Dillingen |
| DIRO-WStE 285 | DIROSTAHL, Remscheid |
| FG 29 W | ThyssenKrupp Schulte GmbH, Essen |
| FGP 28 W | ThyssenKrupp Steel Europe AG, Duisburg |
| P275NH | ArcelorMittal Commercial Germany, Cologne |
| P275NH | ThyssenKrupp Steel Europe AG, Duisburg |
| P275NH | Swiss Steel International GmbH, Düsseldorf |
| P275NH | Klöckner Stahl- und Metallhandel GmbH, Bremen |
| SB 29 FW | Salzgitter Flachstahl GmbH, Salzgitter |
| WStE 285 | Hoesch Hohenlimburg GmbH, Hagen |
| WStE 285 | Salzgitter Flachstahl GmbH, Salzgitter |
| WStE 285 | ThyssenKrupp Steel Europe AG, Duisburg |
| WStE 285 | Saarstahl AG, Völklingen |
| WStE 285 | Georgsmarienhütte GmbH, Georgsmarienhütte |
| WStE 285 | Swiss Steel International GmbH, Düsseldorf |
| WStE 285 | Bochumer Verein Verkehrstechnik GmbH, Bochum |
| WStE 285 | Klöckner Stahl- und Metallhandel GmbH, Bremen |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |