MgAl3Zn | 3.5314 Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Material Description

Material Number	Material Name	Material Number (single)	Standard	Standard Status	Country	VDA 231-106 classification
3.5314 (WL 3.5314 : 1979-11)	MgAl3Zn	3.5314	WL 3.5314 : 1979-11	Valid	Germany	2.2	1)
1) Remark: Low-alloy, weldable magnesium-aluminum-zinc-manganese alloy for aerospace applications with medium strength and good hot forming properties. It is not age-hardenable, has very good machinability, and is susceptible to corrosion in moist, especially saline, atmospheres. Application: - complex shaped extruded sections and die forgings - dimensionally stable semi-finished parts

Chemical Composition

Al [%]	Ca [%]	Cu [%]	Fe [%]	Mn [%]	Ni [%]	Si [%]	Zn [%]	Remainder
blur	blur	blur	blur	blur	blur	blur	blur	blur	1)2)
1) Source: blur
2) Remark: blur

Material Compliance

REACh	RoHS
blur	blur

Mechanical Properties

Semi-finished Product	Condition	Condition Number	Nominal Size [mm]	Temperature [°C]	Specimen Direction	Basis	Tensile Strength [MPa]	Yield Strength (0.2% offset) [MPa]	Elongation A [%]	Compressive Yield Strength (0.2% offset) [MPa]	Shear Strength [MPa]	Hardness HB \| HBW	Ultimate Bearing Strength (e/D=1.5) [MPa]	Ultimate Bearing Strength (e/D=2.0) [MPa]	Bearing Yield Strength (e/D=1.5) [MPa]
blur	blur	blur	blur	blur	blur		blur	blur	blur							1)
blur	blur	blur	blur	blur	blur		blur	blur	blur							1)
blur	blur	blur	blur	blur	blur		blur	blur	blur							1)
blur	blur	blur	blur	blur	blur		blur	blur	blur							1)
blur	blur	blur		blur								blur				1)
blur	blur	blur	blur	blur	blur		blur	blur	blur							2)3)
blur	blur	blur	blur	blur								blur				2)
blur	blur	blur	blur	blur	blur		blur	blur	blur							4)
blur	blur	blur	blur	blur								blur				4)
blur			blur	blur	blur	blur	blur	blur								5)
blur			blur	blur	blur	blur	blur	blur								5)
blur			blur	blur	blur	blur	blur	blur								5)
blur			blur	blur	blur	blur	blur	blur								5)
blur			blur	blur	blur	blur	blur	blur								5)
blur			blur	blur	blur	blur	blur	blur								5)
blur			blur	blur	blur	blur	blur	blur								5)
blur			blur	blur	blur	blur					blur		blur	blur	blur	5)
blur			blur	blur	blur	blur				blur	blur		blur	blur	blur	5)
blur			blur	blur	blur	blur				blur	blur		blur	blur	blur	5)
blur			blur	blur	blur	blur				blur						5)
1) Source: blur
2) Source: blur
3) Remark: blur
4) Source: blur
5) Source: blur

Physical Properties

Temperature [°C]	Melting Temperature [°C]	Density [g/cm³]	Young's Modulus [GPa]	Bulk Modulus [GPa]	Thermal Conductivity [W/(m*K)]	Electric Conductivity [MS/m]
blur		blur	blur	blur		blur	1)
	blur						1)
blur						blur	1)
blur						blur	1)
blur						blur	1)
blur						blur	1)
blur						blur	1)
blur						blur	1)
		blur	blur				2)
blur					blur		2)
1) Source: blur
2) Source: blur

FKM Guideline Fatigue Strength

Stress Ratio	Stress Concentration Factor	Number of Cycles	Fatigue Limit under rev. Tension-Compression Stresses [MPa]
blur	blur	blur	blur	1)
1) Source: blur

Fracture Toughness

Condition	Temperature [°C]	Tensile Strength [MPa]	Plane-Strain Fracture Toughness KIc [MPa*m^½]
blur	blur		blur	1)
blur	blur	blur	blur	1)
1) Source: blur

Welding and Joining

Procedure	Welding and Joining - Evaluation
	blur	1)
blur	blur	1)
blur	blur	1)
1) Source: blur

Cross Reference

Material Name	Country	Standard
3.5314.0	Germany	WL 3.5314-1
3Al-1Zn-0,25Mn	Germany	WL 3.5314-2
MgAl3Zn	Germany	WL 3.5314-3
3.5312	Germany	DIN 1729-1	1)
3.5312	Germany	DIN 9715	1)
MG-P-62	Europe	AECMA	2)
G-A3Z1	France	AIR 9052	1)
P-MgAl3ZnMn	Italy	UNAVIA 812-01	1)
AZ31B	USA	QQ-M-31	1)
AZ31B	USA	QQ-M-40	3)
AZ31B	USA	WW-T-825	4)
B91 Alloy AZ31B	USA	ASTM B91	3)
B107 Alloy AZ31B	USA	ASTM B107	1)
M11312	USA	UNS	2)
3.5312	Germany	DIN 1729-1	1)
1) Source: WL 3.5314-1 : 1979-11
2) Source: OTTO FUCHS KG, Meinerzhagen
3) Source: WL 3.5314-3 : 1979-11
4) Source: WL 3.5314-2 : 1979-11

Producer/Supplier/Trade names

Tradename	Supplier
MA39	OTTO FUCHS KG, Meinerzhagen

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
blur									blur

Density

Temperature [°C]	Density [g/cm³]
blur	blur

Linear-elastic

Temperature [°C]	Young's modulus [GPa]	Bulk modulus [GPa]	Poisson's ratio
blur	blur
blur		blur
blur			blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

0.2% Compressive yield strength

Temperature [°C]	0.2 % Compressive yield strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Thermal conductivity

Temperature [°C]	Thermal conductivity [W/(m*K)]
blur	blur

Designation

Designation	Material number	Source
blur	blur	blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
		blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
		blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
		blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
		blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

0.2% Compressive yield strength

Temperature [°C]	0.2 % Compressive yield strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
		blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

0.2% Compressive yield strength

Temperature [°C]	0.2 % Compressive yield strength [MPa]
blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
		blur	blur						blur

0.2% Compressive yield strength

Temperature [°C]	0.2 % Compressive yield strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur		blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

MgAl3Zn | 3.5314 Material Datasheet

Material Standard Values

Material Models for Simulation

Material Description

Chemical Composition

Material Compliance

Mechanical Properties

Physical Properties

FKM Guideline Fatigue Strength

Fracture Toughness

Welding and Joining

Cross Reference

Producer/Supplier/Trade names

MgAl3Zn (3.5314; WL 3.5314 : 1979-11)

Classification

Density

Linear-elastic

Yield strength

0.2% Compressive yield strength

Tensile strength

Thermal conductivity

Designation

MgAl3Zn (section; 0.000-6.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (section; 38.000-60.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (section; 6.000-38.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (section; 6.000-60.000mm)

Classification

Yield strength

0.2% Compressive yield strength

Tensile strength

MgAl3Zn (section; 60.000-125.000mm)

Classification

Yield strength

0.2% Compressive yield strength

Tensile strength

MgAl3Zn (tube; 0.700-19.000mm)

Classification

0.2% Compressive yield strength

MgAl3Zn (untreated; drop forging; 0.000-75.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (untreated; section; 0.000-6.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (untreated; section; 38.000-60.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (untreated; section; 6.000-38.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (untreated; section; 60.000-125.000mm)

Classification

Yield strength

Tensile strength

MgAl3Zn (untreated; tube; 0.000-20.000mm)

Classification

Yield strength

Tensile strength

Diagram Settings

Diagram Preview

Data Values

Series Points