GX3CrNi13-4 | 1.6982 Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access Best value

Material Description

Material Number Material Name Material Number (single) Standard Scope Standard Status Country Successor VDA 231-106 classification Application temperature [°C]
1.6982 (DIN EN 10213-3 : 1996-01) GX3CrNi13-4 1.6982 DIN EN 10213-3 : 1996-01 DIN EN 10213-3 : 1996-01 replaced by DIN EN 10213 : 2008-01 With DIN EN 10213-1 : 1996-01 partial replacement for DIN 17182 : 1992-05 Replaced Germany GX3CrNi13-4 1.1.2 -120 - 20 1)
1) Remark: Material GX3CrNi13-4 is equivalent to trademark G-X 3 CrNi 13 4 acc. to SEW 685-89. It combines high strength and very good cryogenic properties. It is used at low temperatures in refrigerator construction up to approx. -120 °C. Material G-X 5 CrNi 13 4, material number 1.4313 is acc. to VdTÜV-material specification 452 applicable for pressure vessels acc. to TRB 100 (and AD-data sheets W5 and W10) from -120 to 20 °C. Further application for blade and guide wheels for pumps, compressors and turbines as well as for pump casings and machine components in hydraulic installations from -120 to 20 °C. Further application in the nuclear power engineering if the relevant specifications allow the application at -120 to 20 °C. The welding suitability of the steel cast is examined for the welding methods TIG-welding, metal arc welding and submerged welding. After the welding the material have to cool down under 80 deg. for an following heat-treatment. An double tempering or stress relieve annealing is possible. After the double tempering an decrease of the strength should considered. The cooling rate until below 300 °C should not exceed 80 K/h. By the welding in the production of thin-walled parts its possible to abandon the pre-heating, tempering or stress relieve annealing if appropriate verification was done.

Chemical Composition

C [%] Cr [%] Mn [%] Mo [%] Ni [%] P [%] S [%] Si [%] Remainder
blur blur blur blur blur blur blur blur blur 1)
1) Source: blur

Material Compliance

REACh RoHS
blur blur

Mechanical Properties

Semi-finished Product Condition Nominal Size [mm] Temperature [°C] Tensile Strength [MPa] Yield Strength (0.2% offset) [MPa] Elongation A [%]
blur blur blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Physical Properties

Temperature [°C] Density [g/cm³] Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] Thermal Conductivity [W/(m*K)] Mean Specific Heat Capacity [kJ/(kg*K)] Magnetizeability
blur blur blur blur 1)
blur blur blur 1)
blur blur 1)
1) Source: blur

Toughness Data (Impact)

Condition Nominal Size [mm] Temperature [°C] Specimen Shape Notch Impact Energy [J]
blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Heat Treatment

Heat Treatment Step Temperature [°C] Medium
blur blur blur blur 1)
blur blur blur 1)
blur blur blur 1)
1) Source: blur

Cross Reference

Material Name Country Standard
GS-X 3 CrNi 13 4 Germany SEW 685

Similar Materials

Diagram Settings
Diagram Preview
Select properties and click "Preview Diagram"