EN-GJN-HV600 | EN-JN2049 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full Access Best valueMaterial Description
| Material Number | Material Name | Material Number (single) | Standard | Scope | Standard Status | Country | Predecessor | Successor | VDA 231-106 classification | |
|---|---|---|---|---|---|---|---|---|---|---|
| EN-JN2049 (DIN EN 12513 : 2001-01) | EN-GJN-HV600 | EN-JN2049 | DIN EN 12513 : 2001-01 | DIN EN 12513 : 2001-01 replaced by DIN EN 12513 : 2011-05 | Replaced | Germany | G-X 300 CrNiSi 9 5 2 | EN-GJN-HB555 | 1.2 | 1) |
| 1) Remark: EN-GJN-HV600 consists of eutectical carbides of types M7C3 and M3C (M=Fe, Cr) in a matrix, which contains mostly martensite and sometimes bainite and austenite. The comparable G-X 300 CrNiSi 9 5 2 acc. DIN 1695 : 1981-09 (invalid) is characterised by a high wear resistance and applicable at moderate impact stress. The wear resistance increases with the carbon content while the impact resistance decreases. The correlation between thickness of cast iron and chemical composition exist: - Thickness of cast iron up to 25 mm: Si:1,90%, Mn:0,40%, Ni:4,5%, Cr:8,5% - Thickness of cast iron > 25 bis 50 mm: Si:0,40%, Mn:0,50%, Ni:3,8%, Cr:2,0% - Thickness of cast iron > 50 bis 100 mm: Si:1,80%, Mn:0,50%, Ni:5,0%, Cr:9,0% - Thickness of cast iron > 100 mm: Si:1,60%, Mn:0,60%, Ni:5,5%, Cr:9,5%.. For thicknesses far 100 mm it is recommended to increase the Ni-content. Cast parts made of cast iron with 5 % Ni and 9 % Cr are mostly delivered under heat treated conditions. |
Chemical Composition
| C [%] | Cr [%] | Mn [%] | Ni [%] | P [%] | S [%] | Si [%] | Remainder | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Mechanical Properties
| Temperature [°C] | Hardness HV | |
|---|---|---|
| blur | blur | 1) |
| 1) Source: blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | Holding Time [h] | Medium | |
|---|---|---|---|---|
| blur | blur | blur | blur | 1) |
| 1) Source: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| Grade 2C | Great Britain | BS 4844-86 |
| Grade 2D | Great Britain | BS 4844-86 |
| Grade 2E | Great Britain | BS 4844-86 |
| SIS 0457-00 | Sweden | MNC 708E-71 |
| ÖX 300 CrNiSi9 5 2 | Hungary | MSZ 8273 |
| ID Ni-HiCr | USA | ASTM A 532-87 |
| G-X 300 CrNiSi 9 5 2 (0.9630) | Germany | DIN 1695 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| G-X 300 CrNiSi 9 5 2 | Silbitz Group GmbH, Silbitz |
| G-X 300 CrNiSi 9 5 2 | Procast Guss GmbH, Gütersloh |
| G-X 300 CrNiSi 9 5 2 | GESTAGUSS-GEW Edelstahlgießerei GmbH, Wetterzeube |