EN AW-Al Zn4,5Mg1 | EN AW-7020 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Predecessor | Successor | |
|---|---|---|---|---|---|---|---|---|
| EN AW-7020 (DIN EN 573-3 : 2003-10) | EN AW-7020 | DIN EN 573-3 : 2003-10 | DIN EN 573-3 : 2003-10 replaced by DIN EN 573-3 : 2007-11 | Replaced | Germany | AlZn4,5Mg1 | EN AW-Al Zn4,5Mg1 | 1) |
| 1) Remark: Material EN AW-AlZn4,5 Mg is produced for sheet, strip and plates, for extruded and drawn components. The not food-safe alloy is used for wire and prewire for mechanical applications as well as for forged parts and prematerial. To the comparable mark AlZn4,5Mg1, mat. No.3.4355, acc. to DIN 1725-1 applies: The alloy is a natural and artificial agable aluminium-alloy of mean strength which was developped especially for welding constructions. The material achieves after artificial aging strength values up to 250N/mm² and is therefore suitable for ststicly high strained constructions. Heat-treatment for hardening: solution annealing: 460 to 485 °C, quenching in air natural aging: min. 90 d at RT artificial aging: 8 to 12 h at 90 to 100°C and 16 to 24 h at 140 to 160°C. Natural aged condition is achieved after min. 90 days. It can be also achieved by quenching after press (i.e. without extra solution annealing before natural aging). Artificial aging is an aging treatment in two steps. The advantages of these alloys used for welding constructions are: the alloy is self-acting hardening in the heat-affected zone after welding and it is has a higher corrosion resistance in artificial than in natural aged condition. In the event of corrosive load to welded construction parts has to be a artificial aging after welding. Application: in machine engineering (incl. mold making) for machine solids, cases, rollertubes, machine benches (sections), for appliances (anchor, head and punch unit holder plates) as well as for guide plates and tools, turned parts (hydraulics/ pneumatics). In apparatus and tank construction, for tanks in low-temperature sector, in rail vehicle manufacturing for wagon bodies, equipment and axle bearing cases, in conveyor technics for carrying constructions. In vehicle manufacturing for commercial-vehicle bodies, tank and bulk trucks, motor busses, bumpers and safety parts, in shipbuilding for radar systems resp. equipment as well as in aircraft construction. |
Chemical Composition
| Cr [%] | Cu [%] | Fe [%] | Mg [%] | Mn [%] | Si [%] | Zn [%] | Zr [%] | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||
| 2) Remark: blur |
Mechanical Properties
| Semi-finished Product | Condition | Designation of the delivered Condition DIN | Delivery Condition EN | Nominal Size [mm] | Temperature [°C] | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | Elongation A50 [%] | Hardness HB | HBW | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)7) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)9) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)10) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)11) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)12) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)14) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)9) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)10) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)11) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)12) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)14) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)8) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)9) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)10) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)11) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)12) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)13) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)14) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 15)16) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 15)17) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 15)18) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 15)18) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 19)20) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 19)21) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 18)19) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)23) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)23) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)23) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)24) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)25) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)25) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)25) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)26) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)27) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)27) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)27) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 22)24) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)28) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)30) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)31) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)32) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)33) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)30) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)31) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)32) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)34) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)35) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)36) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)37) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)38) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)39) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)34) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)35) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)36) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)37) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)38) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)39) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)34) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)35) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)36) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)37) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)38) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)29) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 28)39) |
| 1) Source: blur | |||||||||||
| 2) Remark: blur | |||||||||||
| 3) Remark: blur | |||||||||||
| 4) Remark: blur | |||||||||||
| 5) Remark: blur | |||||||||||
| 6) Remark: blur | |||||||||||
| 7) Remark: blur | |||||||||||
| 8) Remark: blur | |||||||||||
| 9) Remark: blur | |||||||||||
| 10) Remark: blur | |||||||||||
| 11) Remark: blur | |||||||||||
| 12) Remark: blur | |||||||||||
| 13) Remark: blur | |||||||||||
| 14) Remark: blur | |||||||||||
| 15) Source: blur | |||||||||||
| 16) Remark: blur | |||||||||||
| 17) Remark: blur | |||||||||||
| 18) Remark: blur | |||||||||||
| 19) Source: blur | |||||||||||
| 20) Remark: blur | |||||||||||
| 21) Remark: blur | |||||||||||
| 22) Source: blur | |||||||||||
| 23) Remark: blur | |||||||||||
| 24) Remark: blur | |||||||||||
| 25) Remark: blur | |||||||||||
| 26) Remark: blur | |||||||||||
| 27) Remark: blur | |||||||||||
| 28) Source: blur | |||||||||||
| 29) Remark: blur | |||||||||||
| 30) Remark: blur | |||||||||||
| 31) Remark: blur | |||||||||||
| 32) Remark: blur | |||||||||||
| 33) Remark: blur | |||||||||||
| 34) Remark: blur | |||||||||||
| 35) Remark: blur | |||||||||||
| 36) Remark: blur | |||||||||||
| 37) Remark: blur | |||||||||||
| 38) Remark: blur | |||||||||||
| 39) Remark: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| 7020 | Belgium | NBN P 21-001 |
| 7020 | France | NF A 50-411 |
| A-Z5G | France | NF A 50-411 |
| 7020 | France | NF A 50-451 |
| A-Z5G | France | NF A 50-451 |
| 7020 | France | NF A 50-901 |
| A-Z5G | France | NF A 50-901 |
| 7020 | Great Britain | BS 4300/14 |
| H17 | Great Britain | BS 4300/14 |
| 7020 | Great Britain | BS 4300/15 |
| H17 | Great Britain | BS 4300/15 |
| AA 7020 | USA | International Registration Record (AA) |
| AlZn4,5Mg1 | International | ISO 209-1 |
| 7020 | Italy | UNI 9007/1 |
| 7791 | Italy | UNI 9007/1 |
| 9007/1 | Italy | UNI 9007/1 |
| P-AlZn4,5Mg1,2MnCr | Italy | UNI 9007/1 |
| 3.7551.00 | Yugoslavia | JUS C.C2.100 |
| AlZn5Mg1 | Yugoslavia | JUS C.C2.100 |
| 17410 | Norway | NS 17001 |
| AlZn4Mg1 | Norway | NS 17001 |
| AlZn4,5Mg1 | Austria | ÖNORM M 3430 |
| 144425 | Sweden | SIS 144425 |
| AlZn4,5Mg1 | Switzerland | SN 210900 |
| 7020 | Spain | UNE 38-300 |
| Al-4Zn1Mg | Spain | UNE 38-300 |
| L-3741 | Spain | UNE 38-300 |
| 7020 | Spain | UNE 38-374 |
| Al-4Zn1Mg | Spain | UNE 38-374 |
| L-3741 | Spain | UNE 38-374 |
| AlZn4,5Mg1 | Turkey | TS 412 |
| UNS A 97020 | USA | UNS |
| AlZn4,5Mg1 (3.4335) | Germany | DIN 1725-1 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| 7120 | Erbslöh Aluminium GmbH, Velbert |
| 721 | Erbslöh Aluminium GmbH, Velbert |
| 7350 | Novelis AG, Koblenz |
| Alcan WG-D 74 S | Novelis Deutschland GmbH, Göttingen |
| AZ 14 | OTTO FUCHS KG, Meinerzhagen |
| EN AW-Al Zn4,5Mg1 | F. Hackländer GmbH, Kassel |
| EN AW-Al Zn4,5Mg1 | Drahtwerk Elisental W. Erdmann GmbH & Co, Neuenrade |
| EN AW-Al Zn4,5Mg1 | CUMSAL GmbH, Wilnsdorf |
| EN AW-Al Zn4,5Mg1 | CSN Carl Schreiber GmbH, Neunkirchen |
| EN AW-Al Zn4,5Mg1 | Wieland Prometa GmbH, Düsseldorf |
| EN AW-Al Zn4,5Mg1 | Manfred J.C. Niemann, Bremen |
| EN AW-Al Zn4,5Mg1 F35 | Hydro Aluminium Extrusion Deutschland GmbH, Rackwitz |
| VAW 21/51 | Hydro Aluminium Rolled Products GmbH, Grevenbroich |
| VAW 21/51 | Hydro Aluminium Deutschland GmbH, Hannover |
| VAW 21/51 | Aluminium Norf GmbH, Neuss |
| VAW 21/51 | Hydro Aluminium Deutschland GmbH , Bonn |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |