CuNi2Si | CW111C Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access

Material Description

Material Number Material Number (single) Standard Range of Application Standard Status Country Predecessor Successor
CW111C (DIN EN 12167 : 2011-08) CW111C DIN EN 12167 : 2011-08 DIN EN 12167 : 2011-08 replaced by DIN EN 12167 : 2016-11 Replaced Germany CuNi2Si CuNi2Si 1)
1) Remark: CuNi2Si, mat. No CW111C, is counted among hardenable, low alloyed copper alloys. To the comparable make CuBNi2Si, mat. No 2.0855, acc. to DIN 17666 : 1983-12 applies: The material shows favorable electrical and thermal conductivity, corrosion resistance, high fatigue and creep resistance as well as favorable spring properties. CuNi2Si is in hardened condition resistant to stress corrosion. Temperature for removal of workhardening approximates 450°C. Strength still increases at low-temperature range. Processing properties: hot and cold forming: good machinability: moderately soft soldering: good hard soldering: moderately gas shielded welding: moderately burnishing: good Application: Particularly for aerial line material, such as clamps, mounting links, nuts, high-strength and corrosion resistant screws. Furthermore for wire ropes in electrical overhead line construction, bearing bushings, roller bearing cages, valve guide bushings and springs. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5)

Chemical Composition

Fe [%] Mn [%] Ni [%] Pb [%] Si [%]
blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Mechanical Properties

Semi-finished Product Strength Abbrevation Nominal Size [mm] Temperature [°C] Tensile Strength [MPa] Yield Strength (0.2% offset) [MPa] Elongation A100 [%] Elongation A11,3 [%] Elongation A [%] Hardness HB | HBW
blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur 1)
1) Source: blur

Physical Properties

Condition Temperature [°C] Melting Temperature [°C] Density [g/cm³] Young's Modulus [GPa] Poisson's Ratio Mean Coefficient of Thermal Expansion [10^-6*K^-1] Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] Thermal Conductivity [W/(m*K)] Mean Specific Heat Capacity [kJ/(kg*K)] Electric Conductivity [MS/m] Specific Electric Conductivity [% IACS]
blur blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur blur 3)
blur blur blur blur blur blur blur blur blur blur blur blur 3)
blur blur blur blur blur blur blur blur blur blur blur blur 4)
blur blur blur blur blur blur blur blur blur blur blur blur 4)
1) Source: blur
2) Source: blur
3) Source: blur
4) Source: blur

Heat Treatment

Heat Treatment Temperature [°C]
blur blur 1)
blur blur 1)
blur blur 1)
1) Source: blur

Cross Reference

Material Name Country Standard
CuNi2Si Europe EN 12167
CuNi2Si International ISO 1187 1)
C18000 USA UNS 1)
C64700 USA UNS 1)
B411 UNS C64700 USA ASTM B411 1)
2.0855 Germany DIN 17666 2)
CuNi2Si Germany DIN 17666 2)
1) Source: Deutsches Kupferinstitut Berufsverband e.V., Düsseldorf
2) Source: DIN CEN/TS 13388 (DIN SPEC 9700)

Material Compliance

REACh RoHS
blur blur

Linear-elastic

Temperature [°C] Young's modulus [GPa] Bulk modulus [GPa] Shear modulus [GPa] Poisson's ratio
blur blur blur blur blur
blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Coefficient thermal expansion

Related Temperature [°C] Temperature [°C] Coefficient thermal expansion [10^-6*K^-1]
blur blur blur

Specific heat

Temperature [°C] Specific heat [kJ/(kg*K)]
blur blur

Density

Temperature [°C] Density [g/cm³]
blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Thermal conductivity

Temperature [°C] Thermal conductivity [W/(m*K)]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Designation

Designation Material number Source
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Linear-elastic

Temperature [°C] Young's modulus [GPa] Bulk modulus [GPa] Shear modulus [GPa] Poisson's ratio
blur blur blur blur blur

Thermal conductivity

Temperature [°C] Thermal conductivity [W/(m*K)]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur