C50E | 1.1206 Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Material Description

Material Number	Material Name	Material Number (single)	Standard	Scope	Standard Status	Country	Predecessor	Successor	VDA 231-106 classification	Application temperature [°C]
1.1206 (DIN EN 10083-1 : 1996-10)	C50E	1.1206	DIN EN 10083-1 : 1996-10	DIN EN 10083-1 : 1996-10 replaced by DIN EN 10083-1/-2 : 2006-10 and DIN EN 10083-3 : 2007-01	Replaced	Germany	Ck 50	C50E	1.1.1	≥ -25	1)
1) Remark: Steel C50E is suitable for larger parts (heavy forged parts) in vehicle manufacturing, engine and machine engineering (e.g. transmission parts, shafts, wheel hubs). Lowest working temperature -25 °C. As a bright steel product it is used in the form of bars, bright, straight, in different conditions (see DIN EN 10277).

Chemical Composition

C [%]	Cr [%]	Mn [%]	Mo [%]	Ni [%]	P [%]	S [%]	Si [%]	Cr+Mo+Ni [%]	Remainder
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur	1)
1) Source: blur

Material Compliance

REACh	RoHS
blur	blur

Mechanical Properties

Semi-finished Product	Condition	Nominal Size [mm]	Temperature [°C]	Tensile Strength [MPa]	Yield Strength [MPa]	Elongation A [%]	Reduction of Area [%]	Hardness HB \| HBW	Hardness HRC	Hardness HV
blur	blur	blur	blur	blur	blur	blur	blur				1)2)
blur	blur	blur	blur	blur	blur	blur	blur				1)2)
blur	blur	blur	blur	blur	blur	blur	blur				1)2)
blur	blur	blur	blur	blur	blur	blur	blur				1)3)
blur	blur	blur	blur	blur	blur	blur	blur				1)3)
blur	blur	blur	blur	blur	blur	blur	blur				1)3)
blur	blur	blur	blur	blur	blur	blur					1)4)
blur	blur	blur	blur	blur	blur	blur					1)4)
blur	blur	blur	blur	blur	blur	blur					1)4)
	blur		blur					blur			5)6)
blur	blur	blur	blur							blur	5)
blur	blur							blur			1)7)
blur	blur							blur			1)7)
	blur	blur							blur		1)8)
1) Source: blur
2) Remark: blur
3) Remark: blur
4) Remark: blur
5) Source: blur
6) Remark: blur
7) Remark: blur
8) Remark: blur

Hardenability (Jominy test)

Condition	Front Distance [mm]	Hardness HRC (+H grade)	Hardness HRC (+HH grade)	Hardness HRC (+HL grade)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur	blur			1)2)
blur	blur		blur		1)3)
blur	blur		blur		1)4)
blur	blur		blur		1)4)
blur	blur			blur	1)5)
blur	blur			blur	1)6)
blur	blur			blur	1)6)
1) Source: blur
2) Remark: blur
3) Remark: blur
4) Remark: blur
5) Remark: blur
6) Remark: blur

Heat Treatment

Heat Treatment	Step	Temperature [°C]	Holding Time [h]	Medium
blur		blur	blur		1)
blur	blur	blur			1)
blur	blur	blur	blur	blur	1)2)
blur	blur	blur	blur		1)
1) Source: blur
2) Remark: blur

Cross Reference

Material Name	Country	Standard
50	China	GB 699
C50E	Europe	EN 10083-2
080M50	Great Britain	BS 970/1
C50E4	International	ISO 683-1
C50	Italy	UNI 7845
S 50 C	Japan	JIS G 4051
1674	Sweden	MNC 852 E
1049	USA	ASTM A 29
1049	USA	ASTM A 108
1049	USA	ASTM A 576
1050	USA	ASTM A 29
1050	USA	ASTM A 108
1050	USA	ASTM A 576
Ck 50	Germany	DIN 17200

Producer/Supplier/Trade names

Tradename	Supplier
1.1206	Platestahl Umformtechnik GmbH, Lüdenscheid
1.1206	ET Edelstahl-Trading GmbH, Willich
1.1206	DWK Drahtwerk Köln GmbH, Köln
BGH 1206	BGH Edelstahl Siegen GmbH
C50E	AG der Dillinger Hüttenwerke, Dillingen
C50E	Salzgitter Flachstahl GmbH, Salzgitter
C50E	ThyssenKrupp Steel Europe AG, Duisburg
C50E	Saarstahl AG, Völklingen
C50E	Swiss Steel International GmbH, Düsseldorf
C50E	Stahlwerk Unna GmbH & Co.KG, Unna
C50E	C.D. Wälzholz GmbH & Co. KG, Hagen
C50E	Schmiedewerke Gröditz GmbH, Gröditz
C50E	Stahlwerk Annahütte Max Aicher GmbH & Co. KG, Hammerau
C50E	voestalpine AG, Linz
C50E	HEINE + BEISSWENGER Stiftung + Co.KG, Fellbach
C50E	Tata Steel, IJmuiden
C50E	Hammerwerk Erft, G. Diederichs GmbH & Co. KG, Bad Münstereifel-Arloff
C50E	Swiss Steel AG, Emmenbrücke
C50E	ORI MARTIN Deutschland GmbH, Duisburg
C50E	Deutsche Edelstahlwerke Specialty Steel GmbH & Co. KG, Siegen
Ck 50	ASCOMETAL GmbH, Erkrath
DIRO-C50E	DIROSTAHL, Remscheid
THYROFORT C50E	Deutsche Edelstahlwerke Specialty Steel GmbH & Co. KG, Witten

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
blur									blur

Linear-elastic

Temperature [°C]	Young's modulus [GPa]	Poisson's ratio
blur	blur
blur	blur
blur	blur
blur	blur
blur		blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Alternating stress

Temperature [°C]	Stress ratio	Alternating stress [MPa]	Cycles
blur	blur	blur	blur
blur	blur	blur	blur
blur	blur	blur	blur

Designation

Designation	Material number	Source
blur	blur	blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur
blur		blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
	blur	blur	blur						blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur			blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

C50E | 1.1206 Material Datasheet

Material Test Series Values

Material Standard Values

Material Models for Simulation

Material Description

Chemical Composition

Material Compliance

Mechanical Properties

Hardenability (Jominy test)

Heat Treatment

Cross Reference

Producer/Supplier/Trade names

C50E (1.1206; DIN EN 10083-1 : 1996-10)

Classification

Linear-elastic

Yield strength

Tensile strength

Alternating stress

Designation

C50E (normalized or normalized formed (+N); forging; 0.000-16.000mm)

Classification

Yield strength

Tensile strength

C50E (normalized or normalized formed (+N); forging; 100.000-250.000mm)

Classification

Yield strength

Tensile strength

C50E (normalized or normalized formed (+N); forging; 16.000-100.000mm)

Classification

Yield strength

Tensile strength

C50E (quenched and tempered (+QT); drop forging; 0.000-16.000mm)

Classification

Yield strength

Tensile strength

C50E (quenched and tempered (+QT); drop forging; 16.000-40.000mm)

Classification

Yield strength

Tensile strength

C50E (quenched and tempered (+QT); drop forging; 40.000-100.000mm)

Classification

Yield strength

Tensile strength

C50E (quenched and tempered (+QT); wide flat; 0.000-8.000mm)

Classification

Yield strength

Tensile strength

C50E (quenched and tempered (+QT); wide flat; 20.000-60.000mm)

Classification

Yield strength

Tensile strength

C50E (quenched and tempered (+QT); wide flat; 8.000-20.000mm)

Classification

Yield strength

Tensile strength

Similar Materials

Diagram Settings

Diagram Preview

Data Values

Series Points