C15E | 1.1141 Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access

Material Description

Material Number Material Number (single) Standard Range of Application Standard Status Country Predecessor
1.1141 (DIN EN ISO 683-3 : 2022-06) 1.1141 DIN EN ISO 683-3 : 2022-06 Supersedes DIN EN ISO 683-3 : 2019-04 Valid Germany C15E 1)
1) Remark: Steel C15E is suitable for parts of slightly higher core strength, increased wear strain as well as of higher dimension and complexer form than standard mark C15 in vehicle manufacturing and machine engineering (e.g. levers, joints, gear wheels).

Chemical Composition

C [%] Cr [%] Cu [%] Mn [%] Mo [%] Ni [%] P [%] S [%] Si [%]
blur blur blur blur blur blur blur blur blur 1)
1) Source: blur

Mechanical Properties

Semi-finished Product Condition Nominal Size [mm] Temperature [°C] Tensile Strength [MPa] Yield Strength [MPa] Elongation A [%] Reduction of Area [%] Hardness HB | HBW
blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 3)
blur blur blur blur blur blur blur blur blur 3)
1) Source: blur
2) Remark: blur
3) Source: blur

Physical Properties

Temperature [°C] Density [g/cm³] Young's Modulus [GPa] Shear Modulus [GPa] Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] Differential Coefficient of Thermal Expansion [10^-6*K^-1] Thermal Conductivity [W/(m*K)] Thermal Diffusivity [10^-6 m²/s] Specific Electrical Resistance [µΩm] Mean Specific Heat Capacity [kJ/(kg*K)] True Specific Heat Capacity [kJ/(kg*K)]
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
1) Source: blur
2) Source: blur

Heat Treatment

Heat Treatment Temperature [°C] Holding Time [h]
blur blur blur 1)
blur blur blur 1)
blur blur blur 1)
blur blur blur 1)
blur blur blur 1)
1) Source: blur

Cross Reference

Material Name Country Standard
15 China GB/T 699 1)
15 China GB/T 710 1)
15 China GB/T 3275 1)
U20152 China ISC 1)
1.1141 Europe EN 10084 2)
C15E Europe EN 10084 2)
C15E Europe EN ISO 683-3
15C8 India IS 4432 1)
C15E International ISO 683-3
S15C Japan JIS G 4052 2)
15 Russia GOST 1050 1)
SM15C South Korea KS D 3752 1)
SM15CK South Korea KS D 3752 1)
1015 USA SAE J 403 1)
A576 Grade 1015 USA ASTM A576 1)
A576 Grade 1016 USA ASTM A576 1)
G10150 USA UNS 1)
Ck 15 Germany 1)
1) Source: Stahlschlüssel 2019, Verlag Stahlschlüssel Wegst GmbH, Marbach
2) Source: EN ISO 683-3:2022-02

Producer/Supplier/Trade names

Tradename Supplier
C15E Georgsmarienhütte GmbH, Georgsmarienhütte 1)
C15E HEINE + BEISSWENGER Stiftung + Co.KG, Fellbach 1)
C15E Saarstahl AG, Völklingen 1)
C15E Stahlwerk Annahütte Max Aicher GmbH & Co. KG, Hammerau 1)
C15E ThyssenKrupp Schulte GmbH, Essen 1)
1) Source: Stahlschlüssel 2016, Verlag Stahlschlüssel Wegst GmbH, Marbach

Material Compliance

REACh RoHS
blur blur

FKM Guideline Fatigue Strength

Semi-finished Product Condition Nominal Size [mm] Tensile Strength [MPa] Yield Strength [MPa] Fatigue Limit under rev. Tension-Compression Stresses [MPa] Fatigue Strength under pulsating Tensile Stresses [MPa] Bending Fatigue Strength [MPa] Shear Fatigue Strength [MPa] Torsion Fatigue Strength [MPa] Constant a for size factor Kd for yield stress Rp Constant a for size factor Kd for tensile strength Rm
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Linear-elastic

Temperature [°C] Young's modulus [GPa] Bulk modulus [GPa] Shear modulus [GPa] Poisson's ratio
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur

Alternating stress

Temperature [°C] Stress ratio Mean stress [MPa] Alternating stress [MPa] Cycles
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Electrical resistivity

Temperature [°C] Specific electrical resistance [µΩm]
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur

Coefficient thermal expansion

Related Temperature [°C] Temperature [°C] Coefficient thermal expansion [10^-6*K^-1]
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur

Specific heat

Temperature [°C] Specific heat [kJ/(kg*K)]
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur

Density

Temperature [°C] Density [g/cm³]
blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Thermal conductivity

Temperature [°C] Thermal conductivity [W/(m*K)]
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Designation

Designation Material number Source
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur