C 22.8 | 1.0460 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Name | Material Number (single) | Standard | Scope | Standard Status | Country | Successor | VDA 231-106 classification | |
|---|---|---|---|---|---|---|---|---|---|
| 1.0460 (DIN 17243 : 1987-06) | C 22.8 | 1.0460 | DIN 17243 : 1987-06 | DIN 17243 : 1987-06 replaced by DIN EN 10222-1 : 2002-07, DIN EN 10222-2 : 2000-04, DIN EN 10273 : 2000-04 | Replaced | Germany | P250GH | 1.1.1 | 1) |
| 1) Remark: High temperature steel. Application for shapes and flanges. |
Chemical Composition
| Al [%] | C [%] | Cr [%] | Mn [%] | P [%] | S [%] | Si [%] | Remainder | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Differential Coefficient of Thermal Expansion [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Thermal Diffusivity [10^-6 m²/s] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | True Specific Heat Capacity [kJ/(kg*K)] | |
|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| 1) Source: blur | ||||||||||
| 2) Source: blur |
Toughness Data (Impact)
| Condition | Nominal Size [mm] | Temperature [°C] | Specimen Shape | Specimen Direction | Notch Impact Energy [J] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Welding and Joining
| Procedure | Welding and Joining - Evaluation | Nominal Size [mm] | Preheating [°C] | Added Materials | Information | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Creep Rupture Behaviour
| Temperature [°C] | Creep Tensile Strength at 10^4 h [MPa] | Creep Tensile Strength at 10^5 h [MPa] | Creep Tensile Strength at 2*10^5 h [MPa] | 1% Creep Limit at 10^4 h [MPa] | 1% Creep Limit at 10^5 h [MPa] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||
| 2) Remark: blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | |
|---|---|---|
| blur | blur | 1) |
| blur | blur | 1)2) |
| 1) Source: blur | ||
| 2) Remark: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| CC 20 | France | NF A 35-551 |
| 221-430 | Great Britain | BS 1503 |
| 20 | Russia | GOST 1050 |
| F 13 | International | ISO 2604/1-75 |
| SFV 1 | Japan | JIS G 3211 |
| 20 | Poland | PN 84019 |
| 60+70 | USA | ASTM A 181 |
| P250GH | Germany | DIN EN 10273 |