35CrMo4 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Name | Standard | Standard Status | Country | VDA 231-106 classification | |
|---|---|---|---|---|---|---|
| FE-PL1503 (DIN EN 2446 : 2009-07) | 35CrMo4 | DIN EN 2446 : 2009-07 | Valid | Germany | 1.1.1 | 1) |
| 1) Remark: Low alloy quenched and tempered steel FE-PL1503 (35CrMo4) in the form of bars with tensile strength from 1100-1300 MPa up to 25mm for general aerospace applications. |
Chemical Composition
| C [%] | Cr [%] | Mn [%] | Mo [%] | Ni [%] | P [%] | S [%] | Si [%] | Remainder | |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | Hardness HB | HBW | Hardness HV | |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | |||||||||
| 2) Remark: blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Shear Modulus [GPa] | Poisson's Ratio | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Differential Coefficient of Thermal Expansion [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Thermal Diffusivity [10^-6 m²/s] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | True Specific Heat Capacity [kJ/(kg*K)] | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6) |
| 1) Source: blur | ||||||||||||
| 2) Source: blur | ||||||||||||
| 3) Remark: blur | ||||||||||||
| 4) Source: blur | ||||||||||||
| 5) Remark: blur | ||||||||||||
| 6) Source: blur |
Toughness Data (Impact)
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Shape | Notch Impact Energy [J] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Hardenability (Jominy test)
| Condition | Front Distance [mm] | Hardness HRC | |
|---|---|---|---|
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| 1) Source: blur |
FKM Guideline Fatigue Strength
| Semi-finished Product | Condition | Nominal Size [mm] | Tensile Strength [MPa] | Yield Strength [MPa] | Fatigue Limit under rev. Tension-Compression Stresses [MPa] | Fatigue Strength under pulsating Tensile Stresses [MPa] | Bending Fatigue Strength [MPa] | Shear Fatigue Strength [MPa] | Torsion Fatigue Strength [MPa] | Constant a for size factor Kd for yield stress Rp | Constant a for size factor Kd for tensile strength Rm | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||||||
| 2) Remark: blur |
Fracture Toughness
| Temperature [°C] | Yield Strength [MPa] | Plane-Strain Fracture Toughness KIc [MPa*m^½] | |
|---|---|---|---|
| blur | blur | blur | 1) |
| blur | blur | blur | 2) |
| 1) Source: blur | |||
| 2) Source: blur |
Heat Treatment
| Heat Treatment | Step | Temperature [°C] | Medium | |
|---|---|---|---|---|
| blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | 1) |
| 1) Source: blur |
Cross Reference
| Material Name | Country | Standard | |
|---|---|---|---|
| 35CrMo | China | GB/T 3077 | 1) |
| A30352 | China | GB/T 3077 | 1) |
| FE-PL1503 | Europe | EN 2446 | |
| 1.7220 | Europe | ISO 683-2 | 1) |
| 34CrMo4 | Europe | ISO 683-2 | 1) |
| 35CD4 | France | AIR 9160 | 1) |
| EN2446 A | 2) | ||
| EN2446 U | 2) | ||
| 1) Source: Stahlschlüssel 2019, Verlag Stahlschlüssel Wegst GmbH, Marbach | |||
| 2) Source: EN 2446 |
Producer/Supplier/Trade names
| Tradename | Supplier | |
|---|---|---|
| Aerodur 7220 | Deutsche Edelstahlwerke Specialty Steel GmbH & Co. KG, Witten | 1) |
| 34CrMo4 | HEINE + BEISSWENGER Stiftung + Co.KG, Fellbach | 1) |
| 1.7220 | INTERSTAHL Service GmbH, Wetter | 1) |
| Aerodur 7220 | Swiss Steel International GmbH, Düsseldorf | 1) |
| 1) Source: Stahlschlüssel 2019, Verlag Stahlschlüssel Wegst GmbH, Marbach |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Coefficient thermal expansion
| Related Temperature [°C] | Temperature [°C] | Coefficient thermal expansion [10^-6*K^-1] |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |