15 Mo 3 | 1.5415 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Name | Material Number (single) | Standard | Scope | Standard Status | Country | VDA 231-106 classification | Application temperature [°C] | |
|---|---|---|---|---|---|---|---|---|---|
| 1.5415 (DIN 17155 : 1983-10) | 15 Mo 3 | 1.5415 | DIN 17155 : 1983-10 | DIN 17155 : 1983-10 replaced by DIN EN 10028-1/-2 : 2003-09 | Replaced | Germany | 1.1.1 | ≤ 530 | 1) |
| 1) Remark: High temperature steel for the pressure vessel and steam boiler construction up to 530 °C continuous operation. Application: in the pressure vessel and steam vessel construction for vaporiser tubes, tubes, collector tubes, heat exchanger, pre welded collars, flanges |
Chemical Composition
| C [%] | Cr [%] | Cu [%] | Mn [%] | Mo [%] | P [%] | S [%] | Si [%] | Remainder | |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | Hardness HB | HBW | |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 2)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)6) |
| 1) Source: blur | |||||||||
| 2) Source: blur | |||||||||
| 3) Remark: blur | |||||||||
| 4) Remark: blur | |||||||||
| 5) Remark: blur | |||||||||
| 6) Remark: blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Shear Modulus [GPa] | Poisson's Ratio | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Differential Coefficient of Thermal Expansion [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Thermal Diffusivity [10^-6 m²/s] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | True Specific Heat Capacity [kJ/(kg*K)] | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3)4) |
| 1) Source: blur | ||||||||||||
| 2) Source: blur | ||||||||||||
| 3) Source: blur | ||||||||||||
| 4) Remark: blur |
Welding and Joining
| Procedure | Welding and Joining - Evaluation | Nominal Size [mm] | Preheating [°C] | Added Materials | Information | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Creep Rupture Behaviour
| Semi-finished Product | Temperature [°C] | Creep Tensile Strength at 10^4 h [MPa] | Creep Tensile Strength at 10^5 h [MPa] | Creep Tensile Strength at 2*10^5 h [MPa] | 1% Creep Limit at 10^4 h [MPa] | 1% Creep Limit at 10^5 h [MPa] | |
|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | blur | blur | blur | 2)3) |
| 1) Source: blur | |||||||
| 2) Remark: blur | |||||||
| 3) Source: blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | |
|---|---|---|
| blur | blur | 1) |
| blur | blur | 1) |
| blur | blur | 1) |
| 1) Source: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| 16 Mo 3 | Belgium | NBN 629 |
| 15 D 3 | France | NF A 36-206 |
| 243 | Great Britain | BS 3606 |
| P 26 | International | ISO 2604/4-75 |
| 16 Mo 3 | Italy | UNI 5869 |
| SB 46 M | Japan | JIS G 3103 |
| 15 Mo 3 KK | Austria | M 3121 |
| 16 M | Poland | PN H-84024 |
| 2912 | Sweden | SS |
| F.2601-16 Mo 3 | Spain | UNE 36087 |
| Grade A | USA | ASTM A 204 |
| 16Mo3 | Germany | DIN EN 10028-2 |