14NiCr14 | 1.5752 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Name | Material Number (single) | Standard | Scope | Standard Status | Country | VDA 231-106 classification | |
|---|---|---|---|---|---|---|---|---|
| 1.5752 (WL 1.5752 : 2006-12) | 14NiCr14 | 1.5752 | WL 1.5752 : 2006-12 | Supersedes WL 1.5752 : 1975-05 | Valid | Germany | 1.1.1 | 1) |
| 1) Remark: The case-hardened steel 14NiCr14 for defence industry is used for high loaded coupling and gear parts. The steel has a high core strength, a good toughness and is weldable. |
Chemical Composition
| C [%] | Cr [%] | Mn [%] | Ni [%] | P [%] | S [%] | Si [%] | Remainder | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Mechanical Properties
| Semi-finished Product | Condition | Condition Number | Nominal Size [mm] | Specimen Direction | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | Reduction of Area [%] | Hardness HB | HBW | |
|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Shear Modulus [GPa] | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Mean Specific Heat Capacity [kJ/(kg*K)] | |
|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | 2) |
| 1) Source: blur | |||||||
| 2) Source: blur |
Toughness Data (Impact)
| Condition | Condition Number | Temperature [°C] | Specimen Shape | Specimen Direction | Notch Impact Energy [J] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Hardenability (Jominy test)
| Condition | Front Distance [mm] | Hardness HRC | |
|---|---|---|---|
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| 1) Source: blur |
FKM Guideline Fatigue Strength
| Semi-finished Product | Condition | Nominal Size [mm] | Tensile Strength [MPa] | Yield Strength [MPa] | Fatigue Limit under rev. Tension-Compression Stresses [MPa] | Fatigue Strength under pulsating Tensile Stresses [MPa] | Bending Fatigue Strength [MPa] | Shear Fatigue Strength [MPa] | Torsion Fatigue Strength [MPa] | Constant a for size factor Kd for yield stress Rp | Constant a for size factor Kd for tensile strength Rm | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||||||
| 2) Remark: blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | Medium | |
|---|---|---|---|
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| blur | blur | blur | 1) |
| 1) Source: blur |
Cross Reference
| Material Name | Country | Standard | |
|---|---|---|---|
| 15NiCr13 | Europe | EN 10084 | 1) |
| X 3312 | Australia | AS/NZS 1444 | 1) |
| X 9315 | Australia | AS/NZS 1444 | 1) |
| 13Ni14Cr3 | India | IS 11169 P1 | 1) |
| SNC815 | Japan | JIS G 3509-1 | 1) |
| SNC815 | Japan | JIS G 4052 | 1) |
| SNC815 | Japan | JIS G 4053 | 1) |
| SNC815 | South Korea | KS D 3754 | 1) |
| SNC815 | South Korea | KS D 3867 | 1) |
| A646 Grade 3310 | USA | ASTM A646 | 1) |
| A837 Grade E3310 | USA | ASTM A837 | 1) |
| A914 Grade 3310RH | USA | ASTM A914 | 1) |
| G33106 | USA | UNS | 1) |
| 1.5752.2 | Germany | BWB WL 1.5752 | |
| 1.5752.5 | Germany | BWB WL 1.5752 | |
| 1) Source: Stahlschlüssel 2019, Verlag Stahlschlüssel Wegst GmbH, Marbach |
Producer/Supplier/Trade names
| Tradename | Supplier | |
|---|---|---|
| NCAV 2 | AUBERT & DUVAL Deutschland GmbH, München | 1) |
| BGH 5752 | BGH Edelstahl Siegen GmbH | 1) |
| 14NiCr14 | Buderus Edelstahl GmbH, Wetzlar | 1) |
| Carbodur 5752 | Deutsche Edelstahlwerke Specialty Steel GmbH & Co. KG, Witten | 1) |
| DE 5752 | Dörrenberg Edelstahl GmbH, Engelskirchen | 1) |
| BÖHLER M121 | voestalpine BÖHLER Edelstahl GmbH & Co.KG, Kapfenberg | 1) |
| M121 | voestalpine BÖHLER Edelstahl GmbH & Co.KG, Kapfenberg | 1) |
| BÖHLER E200 | voestalpine BÖHLER Edelstahl GmbH & Co.KG, Kapfenberg | 1) |
| E200 | voestalpine BÖHLER Edelstahl GmbH & Co.KG, Kapfenberg | 1) |
| 1) Source: Stahlschlüssel 2019, Verlag Stahlschlüssel Wegst GmbH, Marbach |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Coefficient thermal expansion
| Related Temperature [°C] | Temperature [°C] | Coefficient thermal expansion [10^-6*K^-1] |
|---|---|---|
| blur | blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |