CuCo1Ni1Be | CW103C Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access

Material Description

Material Number Material Number (single) Standard Range of Application Standard Status Country Successor
CW103C (DIN EN 12163 : 1998-04) CW103C DIN EN 12163 : 1998-04 DIN EN 12163 : 1998-04 replaced by DIN EN 12163 : 2011-08 Replaced Germany CuCo1Ni1Be 1)
1) Remark: The material CuCo1Ni1Be , mat. No CW103C is incomparable to a DIN-make. It is used in the form of plates, sheets, stripes, circular blanks, bars, prematerial for forged parts, wires, profiles and forged parts.

Chemical Composition

Be [%] Co [%] Fe [%] Ni [%]
blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Mechanical Properties

Semi-finished Product Condition Strength Abbrevation Nominal Size [mm] Temperature [°C] Tensile Strength [MPa] Yield Strength (0.2% offset) [MPa] Elongation A10 [%] Elongation A100 [%] Elongation A [%] Hardness HB | HBW Hardness HV
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)3)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)3)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)4)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)4)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)4)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)5)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)4)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur blur blur blur 1)4)
blur blur blur blur blur blur blur blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur
3) Remark: blur
4) Remark: blur
5) Remark: blur

Physical Properties

Temperature [°C] Density [g/cm³]
blur blur 1)
1) Source: blur

Cross Reference

Material Name Country Standard
CuCo1Ni1Be Europe EN 12163

Material Compliance

REACh RoHS
blur blur

Linear-elastic

Temperature [°C] Young's modulus [GPa] Bulk modulus [GPa] Shear modulus [GPa] Poisson's ratio
blur blur blur blur blur
blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Density

Temperature [°C] Density [g/cm³]
blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Designation

Designation Material number Source
blur blur blur
blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur