CuAl11Fe6Ni6 | CW308G Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Predecessor | Successor | Remark |
|---|---|---|---|---|---|---|---|---|
| CW308G (DIN EN 12167 : 2011-08) | CW308G | DIN EN 12167 : 2011-08 | DIN EN 12167 : 2011-08 replaced by DIN EN 12167 : 2016-11 | Replaced | Germany | CuAl11Fe6Ni6 | CuAl11Fe6Ni6 | CuAl11Fe6Ni6 (CW308G) is a wrought alloy of high strength, also at increased temperatures. The strength properties of cold formable wrought alloys are primarily dependent on the deformation grade. Tensile strength, yield strength and hardness rise according to the increasing cold forming grade. Elongation after fracture and contraction at fracture are decreasing. Thermal conductivity is reduced by the Al-content, electrical conductivity decreases according to the increasing AL-content. CuAl10Ni5Fe4 has a high strength at high temperatures up to approx. 300°C and a high endurance strength also at corrosion strain. The alloy has a particularly high strength as well as high corrosion and wear resistance to saltwater, sulfite bases and mineral acids. Processing properties: warm forming: good cold forming: unfavorable machinability: moderately soft soldering: unfavorable hard soldering: moderately gas-shielded welding: good burnishing: good The material is used for construction parts of higher strength, higher loaded bearing parts, pivot bearings at impact loading as well as for valves, valve seats, cover plates, link blocks, wear parts, die plates for chipless forming and for hot steam instruments. |
Chemical Composition
| Al [%] | Fe [%] | Mn [%] | Ni [%] | Pb [%] | Si [%] | Sn [%] | Zn [%] | Source | Remark |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Mechanical Properties
| Semi-finished Product | Strength Abbrevation | Temperature [°C] | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A100 [%] | Elongation A11,3 [%] | Elongation A [%] | Hardness HB | HBW | Source |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | Source |
|---|---|---|
| blur | blur | blur |
Cross Reference
| Material Name | Country | Standard | Source |
|---|---|---|---|
| QAl11-6-6 | China | GB/T 5233 | Deutsches Kupferinstitut Berufsverband e.V., Düsseldorf |
| QAl11-6-6 | China | GB/T 4429 | Deutsches Kupferinstitut Berufsverband e.V., Düsseldorf |
| CuAl11Ni6Fe5 | Germany | DIN 17665 | DIN CEN/TS 13388 (DIN SPEC 9700) |
| 2.0978 | Germany | DIN 17665 | DIN CEN/TS 13388 (DIN SPEC 9700) |
| AlBz11Ni | Germany | ||
| CuAl11Ni | Germany |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| 4520 | VDM Metals GmbH, Frankfurt/Main |
| AB 5 S | Wieland Prometa GmbH, Düsseldorf |
| Aeterna W II C | VDM Metals GmbH, Frankfurt/Main |
| Al-Caro 3 | Wieland Prometa GmbH, Düsseldorf |
| CuAl11Ni6Fe5 | CSN Carl Schreiber GmbH, Neunkirchen |
| CuAl11Ni6Fe5 | Schreier Metall GmbH, Erkrath |
| CuAl11Ni6Fe5 | Wieland Prometa GmbH, Düsseldorf |
| EBh | ZOLLERN GmbH & Co. KG, Sigmaringen |
| VB | ZOLLERN GmbH & Co. KG, Sigmaringen |