X6CrNiNb18-10 | 1.4550 Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access

Material Description

Material Number Material Number (single) Standard Range of Application Standard Status Country Predecessor Successor
1.4550 (DIN EN 10217-7 : 2015-01) 1.4550 DIN EN 10217-7 : 2015-01 DIN EN 10217-7 : 2015-01 replaced by DIN EN 10217-7 : 2021-06 Replaced Germany X6CrNiNb18-10 X6CrNiNb18-10 1)
1) Remark: The austenitic steel X6CrNiNb18-10 is available in the solution annealed condition. Welded circular tubes of this steel are used for compression load and for corrosive load at room temperature, low temperatures and elevated temperatures. The material is resistant to intercrystalline corrosion (up to 400 °C) also in the welded condition.

Chemical Composition

C [%] Cr [%] Mn [%] Nb [%] Ni [%] P [%] S [%] Si [%]
blur blur blur blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Mechanical Properties

Semi-finished Product Condition Nominal Size [mm] Temperature [°C] Specimen Direction Tensile Strength [MPa] Yield Strength (0.2% offset) [MPa] Yield Strength (1.0% offset) [MPa] Elongation A [%]
blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur 1)
1) Source: blur
2) Remark: blur

Physical Properties

Temperature [°C] Density [g/cm³] Young's Modulus [GPa] Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] Differential Coefficient of Thermal Expansion [10^-6*K^-1] Thermal Conductivity [W/(m*K)] Thermal Diffusivity [10^-6 m²/s] Specific Electrical Resistance [µΩm] Mean Specific Heat Capacity [kJ/(kg*K)] True Specific Heat Capacity [kJ/(kg*K)] Magnetizeability
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 1)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
blur blur blur blur blur blur blur blur blur blur blur 2)
1) Source: blur
2) Source: blur

Toughness Data (Impact)

Semi-finished Product Condition Nominal Size [mm] Temperature [°C] Specimen Shape Specimen Direction Notch Impact Energy [J]
blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Cross Reference

Material Name Country Standard
06Cr18Ni11Nb China GB/T 24593 1)
S34778 China GB/T 24593 1)
X6CrNiNb18-10 Europe EN 10217-7
04Cr19Ni9Nb40 India IS 11714-5 1)
TP348 India IS 11714-5 1)
SUS347TB Japan JIS G 3463 1)
SUS347HTB Japan JIS G 3463 1)
STS347TB South Korea KS D 3577 1)
347 USA AISI 2)
A249 Type 347 USA ASTM A249 2)
Type 347 USA AISI 2)
S34700 USA UNS 2)
1) Source: Stahlschlüssel 2016, Verlag Stahlschlüssel Wegst GmbH, Marbach
2) Source: Metals & Alloys in the Unified Numbering System, SAE/ASTM, 11th Edition, 2008

Material Compliance

REACh RoHS
blur blur

Linear-elastic

Temperature [°C] Young's modulus [GPa] Bulk modulus [GPa] Shear modulus [GPa] Poisson's ratio
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur

Alternating stress

Temperature [°C] Stress ratio Mean stress [MPa] Alternating stress [MPa] Cycles
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur

Electrical resistivity

Temperature [°C] Specific electrical resistance [µΩm]
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur

Coefficient thermal expansion

Related Temperature [°C] Temperature [°C] Coefficient thermal expansion [10^-6*K^-1]
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur

Specific heat

Temperature [°C] Specific heat [kJ/(kg*K)]
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur

Density

Temperature [°C] Density [g/cm³]
blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Thermal conductivity

Temperature [°C] Thermal conductivity [W/(m*K)]
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Designation

Designation Material number Source
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur

Strain life

Temperature [°C] Static hardening coefficient [MPa] Static hardening exponent Cyclic fatigue strength coefficient [MPa] Cyclic fatigue strength exponent Ductility coefficient [Pa] Ductility exponent Cyclic strength coefficient [MPa] Cyclic strain hardening exponent Young's modulus [GPa]
blur blur blur blur blur blur blur blur blur blur
blur blur blur blur blur blur blur blur blur blur
blur blur blur blur blur blur blur blur blur blur
blur blur blur blur blur blur blur blur blur blur
blur blur blur blur blur blur blur blur blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur