X3CrNiMoAl13-8-2 | 1.4534 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Successor | Application temperature [°C] | |
|---|---|---|---|---|---|---|---|---|
| 1.4534 (WL 1.4534 : 1984-07) | 1.4534 | WL 1.4534 : 1984-07 | WL 1.4534 : 1984-07 replaced by WL 1.4534 : 2012-10 | Replaced | Germany | X3CrNiMoAl13-8-2 | ≤ 315 | 1) |
| 1) Remark: The hardenable chrome-nickel-molybdenum-aluminum steel is resistant to stress corrosion and possesses highest strength up to 315°C. It has a good toughness and tensile strength also in transverse direction and with larger cross sections and it is weldable. |
Chemical Composition
| Al [%] | C [%] | Cr [%] | Mn [%] | Mo [%] | N [%] | Ni [%] | P [%] | S [%] | Si [%] | |
|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Specimen Direction | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A [%] | Reduction of Area [%] | Shear Strength [MPa] | Hardness HB | HBW | Hardness HRC | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)5) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6)7) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6)7) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6)7) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6)7) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6)7) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 6)7) |
| 1) Source: blur | ||||||||||||
| 2) Remark: blur | ||||||||||||
| 3) Remark: blur | ||||||||||||
| 4) Remark: blur | ||||||||||||
| 5) Remark: blur | ||||||||||||
| 6) Source: blur | ||||||||||||
| 7) Remark: blur |
Physical Properties
| Condition | Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Electric Conductivity [MS/m] | Magnetizeability | |
|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Welding and Joining
| Welding and Joining - Evaluation | |
|---|---|
| blur | 1)2) |
| 1) Source: blur | |
| 2) Remark: blur |
Toughness Data (Impact)
| Condition | Temperature [°C] | Specimen Shape | Specimen Direction | Notch Impact Energy [J] | |
|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | 4)5) |
| blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | 4)6) |
| blur | blur | blur | blur | blur | 4)6) |
| 1) Source: blur | |||||
| 2) Remark: blur | |||||
| 3) Remark: blur | |||||
| 4) Source: blur | |||||
| 5) Remark: blur | |||||
| 6) Remark: blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | Holding Time [h] | Medium | |
|---|---|---|---|---|
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 1)3) |
| blur | blur | blur | blur | 1)4) |
| blur | blur | blur | blur | 1)5) |
| blur | blur | blur | blur | 6)7) |
| 1) Source: blur | ||||
| 2) Remark: blur | ||||
| 3) Remark: blur | ||||
| 4) Remark: blur | ||||
| 5) Remark: blur | ||||
| 6) Source: blur | ||||
| 7) Remark: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| S13800 | USA | UNS |
| XM 13 | USA | ASTM A 276 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| 1.4534 | AUBERT & DUVAL Deutschland GmbH, München |
| 1.4534 | BGH Edelstahl Siegen GmbH |
| Böhler N709 VMR | voestalpine BÖHLER Edelstahl GmbH & Co.KG, Kapfenberg |
| 1.4534 | Deutsche Edelstahlwerke Specialty Steel GmbH & Co. KG, Siegen |
| 1.4534 | Enpar Sonderwerkstoffe GmbH, Gummersbach |
| 1.4534 | HEINE + BEISSWENGER Stiftung + Co.KG, Fellbach |
| 1.4534 | Imet Industriemetall Handelsgesellschaft mbH, Hamburg |
| 1.4534 | INTERSTAHL Service GmbH, Wetter |
| 1.4534 | Kind & Co., Edelstahlwerk, Wiehl |
| 1.4534 | pauly STAHLHANDEL, Essen |
| 1.4534 | Platestahl Umformtechnik GmbH, Lüdenscheid |
| 1.4534 | Saarstahl AG, Völklingen |
| 1.4534 | Wuppermann Stahl GmbH, Leverkusen |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Coefficient thermal expansion
| Related Temperature [°C] | Temperature [°C] | Coefficient thermal expansion [10^-6*K^-1] |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |