X 210 Cr 12 | 1.2080 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | Successor | |
|---|---|---|---|---|---|---|---|
| 1.2080 (DIN 17350 : 1980-10) | 1.2080 | DIN 17350 : 1980-10 | DIN 17350 : 1980-10 replaced by DIN EN ISO 4957 : 2001-02 | Replaced | Germany | X210Cr12 | 1) |
| 1) Remark: Properties - high wear resistant, high hardening ability with good dimension stability - medium toughness properties Application: - for high power cutting and stamping tools for sheet thickness up to 3 mm, roll and blade knifes up to 2 mm sheet thickness - draw tools, deep draw tools, jaws for wire pin manufacturing, tools for cold manufacturing of screws, nuts, rivets - dies for cold forming, flanges, bead and truing rolls - form and calibration rolls for the continuous profile and tubing production from strip steel of forming tools in ceramic industry and powder metallurgy - cut-off tools in the paper and plastic industry |
Chemical Composition
| C [%] | Cr [%] | Mn [%] | P [%] | S [%] | Si [%] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Mechanical Properties
| Semi-finished Product | Condition | Hardness HB | HBW | Hardness HRC | |
|---|---|---|---|---|
| blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||
| 2) Remark: blur |
Physical Properties
| Temperature [°C] | Density [g/cm³] | |
|---|---|---|
| blur | blur | 1) |
| 1) Source: blur |
Heat Treatment
| Heat Treatment | Step | Temperature [°C] | Medium | |
|---|---|---|---|---|
| blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | 2)3) |
| blur | blur | blur | blur | 2)3) |
| 1) Source: blur | ||||
| 2) Remark: blur | ||||
| 3) Source: blur |
Cross Reference
| Material Name | Country | Standard | |
|---|---|---|---|
| Cr 12 | China | GB 1299 | |
| 19436 | Czech Republik/Slovakia | CSN 419436 | |
| Z 200 C 12 | France | NF A 35-590 | |
| BD 3 | Great Britain | BS 4659 | |
| Ch 12 | Russia | GOST 5950 | |
| 210 Cr 12 | International | ISO/DIS 4957 | |
| X 210 Cr 12 KU | Italy | UNI 2955/3 | |
| SKD 1 | Japan | JIS G 4404 | |
| NC 11 | Poland | PN 60/H-85023 | |
| 205 Cr 115 | Romania | STAS 3611 | |
| F.5212 | Spain | UNE 36072 | |
| K 1 | Hungary | MSZ 4352/4353 | |
| D 3 | USA | AISI | |
| X210Cr12 | Germany | DIN EN ISO 4957 | |
| 210Cr46 | Germany | TGL 4393 | 1) |
| 1) Source: DIN EN ISO 18265 : 2014-02 |
Producer/Supplier/Trade names
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Fracture Toughness
| Temperature [°C] | Hardness HV | Plane-Strain Fracture Toughness KIc [MPa*m^½] | |
|---|---|---|---|
| blur | blur | blur | 1)2) |
| blur | blur | blur | 1)2) |
| blur | blur | blur | 1)2) |
| blur | blur | blur | 1)2) |
| blur | blur | blur | 1)2) |
| 1) Source: blur | |||
| 2) Remark: blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |