S355ML | 1.8834 Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Scope | Standard Status | Country | Successor | VDA 231-106 classification | |
|---|---|---|---|---|---|---|---|---|
| 1.8834 (DIN EN 10113-3 : 1993-04) | 1.8834 | DIN EN 10113-3 : 1993-04 | DIN EN 10113-3 : 1993-04 replaced by DIN EN 10025-4 : 2005-04 | Replaced | Germany | S355ML | 1.1 | 1) |
| 1) Remark: S355ML is a weldable fine-grained steel with a min. yield point of 355 N/mm². The steel is applicated in thermo mechanical rolled condition for several types of welded constructions such as fixed and movable storage container, high-pressure pipes, bridge and load-bearing constructions. Subsequent heating above 580°C for thermo mechanical rolled products causes reduction of the strength properties. Application limit: at -50°C is warranted a notch impact energy of 27J (longitudinal test specimen). The carbon equivalent (by arrangement) amounts to: for nominal size: < 16 mm: 0,39% > 16 < 40 mm: 0,39% > 40 < 63 mm: 0,40% > 63 < 150 mm: 0,45% Cold forming: Suitability for cold bending, folding, cold flanging or cold welting has to be agreed. For sheet, strip and wide flat steel in thermo mechanical rolled condition, for nominal thickness (s) up to 12 mm can be warranted the following bending radius values: longitudinal: 2,5 x s transverse: 2 x s Sheet and strip of nominal thicknesses < 8 mm for cold forming of sections is available on arrangement (e.g. for production of hollow sections). Warm forming: thermo mechanical rolled products are unsuitable for warm forming. Surface refineability: S355ML has to be suitable by arrangement for hot galnanizing and it has to meet the appropriate product quality requirements. |
Chemical Composition
| Al [%] | C [%] | Mn [%] | Mo [%] | N [%] | Nb [%] | Ni [%] | P [%] | S [%] | Si [%] | Ti [%] | V [%] | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||||||
| 2) Remark: blur |
Mechanical Properties
| Semi-finished Product | Condition | Nominal Size [mm] | Temperature [°C] | Tensile Strength [MPa] | Yield Strength [MPa] | Elongation A [%] | |
|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | |||||||
| 2) Remark: blur |
Toughness Data (Impact)
| Condition | Nominal Size [mm] | Temperature [°C] | Specimen Shape | Specimen Direction | Notch Impact Energy [J] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||
| 2) Remark: blur |
Cross Reference
| Material Name | Country | Standard |
|---|---|---|
| FeE 355 KTTM | Italy | UNI |
| TStE 355 TM | Germany | SEW 083 |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| S355ML | ThyssenKrupp Steel Europe AG, Duisburg |
| XABO 355 T | ThyssenKrupp Steel Europe AG, Duisburg |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
FKM Guideline Fatigue Strength
| Semi-finished Product | Condition | Nominal Size [mm] | Tensile Strength [MPa] | Yield Strength [MPa] | Fatigue Limit under rev. Tension-Compression Stresses [MPa] | Fatigue Strength under pulsating Tensile Stresses [MPa] | Bending Fatigue Strength [MPa] | Shear Fatigue Strength [MPa] | Torsion Fatigue Strength [MPa] | Constant a for size factor Kd for yield stress Rp | Constant a for size factor Kd for tensile strength Rm | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||||||||
| 2) Remark: blur |
Formability - Bending - Folding
| Condition | Nominal Size [mm] | Rolling Direction | Ductility | Bend Factor | |
|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Alternating stress
| Temperature [°C] | Stress ratio | Mean stress [MPa] | Alternating stress [MPa] | Cycles |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |