Compare Plastics, Metals, and More for Construction, Design, and Simulation - Materials Portal

S320GD+AS | 1.0250 Material Datasheet

Material Standard Values
Material Models for Simulation

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access

Material Description

Material Number	Material Number (single)	Standard	Range of Application	Standard Status	Country	Successor	Application temperature [°C]
1.0250 (DIN EN 10154 : 2002-08)	1.0250	DIN EN 10154 : 2002-08	DIN EN 10154 : 2002-08 replaced by DIN EN 10326 : 2004-09 and DIN EN 10327 : 2004-09	Replaced	Germany	S320GD	≤ 700	1)
1) Remark: Structural steel S320GD is produced as: - S320GD+Z (plating Zn) and S 320GD+ZF (plating Zn-Fe- alloy). The zinc-plating (double-sided) amounts to 100, 140, 200, 225, 275, 350, (450), (600) g/m². The bending mandrel diameter accounts for S320GD+Z up to Zn-plating 450 g/m² 3a (a= product thickness). It has to be considered that at hot galvanized products possibly occurs by and by a reduction of reformability. - S320GD+AS (plating aluminium-silicon). The aluminium-silicon plating (double-sided) amounts to 60, 80, 100, 120, 150 g/m². Heat resistance of the AlSi-coating is warranted up to 700°C. The bending mandrel diameter accounts for S320GD+AS 2a (a= product thickness) up to 2,00 mm sheet thickness and 3a for an sheet thickness from 2,0 to 3,0 mm. The material has a min. yield point of 320 N/mm² and is used for high strength and corrosion resistance demands. Application: household appliances industry, construction trade, office furniture industry, electrical industry, car industry. The material acts a substrate for organically coated strips and sheets.

Chemical Composition


1)2)
1) Source: blur
2) Remark: blur

Mechanical Properties

Semi-finished Product	Condition	Nominal Size [mm]	Temperature [°C]	Tensile Strength [MPa]	Yield Strength [MPa]	Elongation A80 [%]
blur	blur	blur	blur	blur	blur	blur	1)2)
1) Source: blur
2) Remark: blur

Producer/Supplier/Trade names

Tradename	Supplier
S320GD+AS	ArcelorMittal Commercial Germany, Cologne
S320GD+AS	Salzgitter Flachstahl GmbH, Salzgitter
S320GD+AS	ThyssenKrupp Steel Europe AG, Duisburg
S320GD+AS	Swiss Steel International GmbH, Düsseldorf
S320GD+AS	voestalpine AG, Linz
S320GD+AS	HEINE + BEISSWENGER Stiftung + Co.KG, Fellbach

Material Compliance

REACh	RoHS
blur	blur

Linear-elastic

Temperature [°C]	Young's modulus [GPa]	Bulk modulus [GPa]	Shear modulus [GPa]	Poisson's ratio
blur	blur	blur	blur	blur
blur	blur	blur	blur	blur
blur	blur	blur	blur	blur
blur	blur	blur	blur	blur
blur	blur	blur	blur	blur

Alternating stress

Temperature [°C]	Stress ratio	Mean stress [MPa]	Alternating stress [MPa]	Cycles
blur	blur	blur	blur	blur
blur	blur	blur	blur	blur
blur	blur	blur	blur	blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur	blur	blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur

Designation

Designation	Material number	Source
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur
blur	blur	blur

Yield strength

Temperature [°C]	0.1% Proof strength [MPa]	0.2% Proof strength [MPa]	Yield strength [MPa]
blur	blur	blur	blur

Tensile strength

Temperature [°C]	Tensile strength [MPa]
blur	blur

Classification

WIAM Material	Treatment	Semi-finished product	Dimension [mm]	Load type	Failure criteria	Rolling direction	Maximum stress [MPa]	Strain at maximum stress [%]	Source description
blur	blur	blur	blur	blur	blur	blur	blur	blur	blur