Materials Portal Logo MATERIALS PORTAL

S280GD+AS | 1.0244 Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access

Material Description

Material Number Material Number (single) Standard Scope Standard Status Country Successor Application temperature [°C] VDA 231-106 classification
1.0244 (DIN EN 10154 : 2002-08) 1.0244 DIN EN 10154 : 2002-08 DIN EN 10154 : 2002-08 replaced by DIN EN 10326 : 2004-09 and DIN EN 10327 : 2004-09 Replaced Germany S280GD ≤ 700 1.1 1)
1) Remark: Structural steel S280GD is produced as: - S280GD+Z (plating Zn) and S 280GD+ZF (plating Zn-Fe- alloy). The zinc-plating (double-sided) amounts to 100, 140, 200, 225, 275, 350, (450), (600) g/m². The bending mandrel diameter accounts for S280GD+Z up to Zn-plating 450 g/m² 1a (a= product thickness). - S280GD+AS (plating aluminium-silicon). The aluminium-silicon plating (double-sided) amounts to 60, 80, 100, 120, 150 g/m². Heat resistance of the AlSi-coating is warranted up to 700°C. The bending mandrel diameter accounts for S280GD+AS 2a (a= product thickness) up to 2,00 mm sheet thickness and 3a for an sheet thickness from 2,0 to 3,0 mm. The material has a min. yield point of 280 N/mm² and is used for high strength and corrosion resistance demands. It has to be considered that possibly occurs by and by a reduction of reformability. The steel of the surface types mentioned is suitable for application of organic platings.

Chemical Composition

1)2)
1) Source: blur
2) Remark: blur

Mechanical Properties

Semi-finished Product Condition Nominal Size [mm] Temperature [°C] Tensile Strength [MPa] Yield Strength [MPa] Elongation A80 [%]
blur blur blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Producer/Supplier/Trade names

Tradename Supplier
S280GD+AS ArcelorMittal Commercial Germany, Cologne
S280GD+AS Hoesch Hohenlimburg GmbH, Hagen
S280GD+AS Salzgitter Flachstahl GmbH, Salzgitter
S280GD+AS ThyssenKrupp Steel Europe AG, Duisburg
S280GD+AS Swiss Steel International GmbH, Düsseldorf
S280GD+AS voestalpine AG, Linz
S280GD+AS HEINE + BEISSWENGER Stiftung + Co.KG, Fellbach
S280GD+AS INTERSTAHL Service GmbH, Wetter

Material Compliance

REACh RoHS
blur blur

Linear-elastic

Temperature [°C] Young's modulus [GPa] Bulk modulus [GPa] Shear modulus [GPa] Poisson's ratio
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur

Alternating stress

Temperature [°C] Stress ratio Mean stress [MPa] Alternating stress [MPa] Cycles
blur blur blur blur blur
blur blur blur blur blur
blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Designation

Designation Material number Source
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur