CuZn39Pb0,5 | CW610N Material Datasheet

Unlock Exclusive Materials Data

Gain access to a wealth of materials data by joining our Materials Portal.

Register for Free or Upgrade for Full Access

Material Description

Material Number Material Number (single) Standard Range of Application Standard Status Country Successor
CW610N (DIN EN 12165 : 1998-04) CW610N DIN EN 12165 : 1998-04 DIN EN 12165 : 1998-04 replaced by DIN EN 12165 : 2011-08 Replaced Germany CuZn39Pb0,5 1)
1) Remark: Material CuZn39Pb0,5, mat. No. CW610N, is an unhardenable wrought alloy. to the comparable make CuZn39Pb0,5, mat. No. 2.0372 acc. to DIN 17660 : 1983-12 applies: High hardness and strength parameter are achievable by cold forming only. Thermal and electrical conductivity are lower than for the unleaded brass grade of the same Zn-content. Machinability is improved by Pb-addition. Corrosion resistance to water, several saline solutions and organic liquids is also lower than for unleaded alloys of the same zinc-content. Processing properties: warm forming: very good cold forming: moderately machinability: good hard soldering: moderately soft soldering: very good TIG-welding: moderately burnishing: very good Application: For plug pins, fitting parts, rivets, condenser plates, floor plate screeding and drawing instruments.

Chemical Composition

Al [%] Cu [%] Fe [%] Ni [%] Pb [%] Sn [%]
blur blur blur blur blur blur 1)2)
1) Source: blur
2) Remark: blur

Mechanical Properties

Semi-finished Product Strength Abbrevation Nominal Size [mm] Temperature [°C] Tensile Strength [MPa] Yield Strength (0.2% offset) [MPa] Hardness HB | HBW Hardness HV
blur blur blur blur blur blur blur blur 1)2)
blur blur blur blur blur blur blur blur 1)3)
blur blur blur blur blur blur blur blur 1)4)
1) Source: blur
2) Remark: blur
3) Remark: blur
4) Remark: blur

Cross Reference

Material Name Country Standard
CuZn39Pb1 Czech Republik/Slovakia CSN 423222
CuZn39Pb0,5 Europe EN 12165
CuZn39Pb0,5 Europe EN 1653
CZ 123 Great Britain BS 2870
CZ 123 Great Britain BS 2871
CZ 123 Great Britain BS 2872
CZ 123 Great Britain BS 2873
CZ 123 Great Britain BS 2874
CZ 123 Great Britain BS 2875
CuZn37Pb1 International ISO 426/2-83
CuZn37Pb2 International ISO 426/2-83
CuZn39Pb1 Romania STAS 95-80
CuZn39Pb1 Hungary MSZ 770/1-77
C36500 USA UNS
C36500 USA ASME SB-171
C36500 USA ASTM B 124
C36500 USA ASTM B 171
C36500 USA ASTM B 283
C36500 USA ASTM B 432
CuZn39Pb0,5 (2.0372) Germany DIN 17660

Material Compliance

REACh RoHS
blur blur

Linear-elastic

Temperature [°C] Young's modulus [GPa] Bulk modulus [GPa] Shear modulus [GPa] Poisson's ratio
blur blur blur blur blur
blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Designation

Designation Material number Source
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur
blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur

Yield strength

Temperature [°C] 0.1% Proof strength [MPa] 0.2% Proof strength [MPa] Yield strength [MPa]
blur blur blur blur

Tensile strength

Temperature [°C] Tensile strength [MPa]
blur blur

Classification

WIAM Material Treatment Semi-finished product Dimension [mm] Load type Failure criteria Rolling direction Maximum stress [MPa] Strain at maximum stress [%] Source description
blur blur blur blur blur blur blur blur blur blur