CuSn8 | CW453K Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Scope | Standard Status | Country | Predecessor | Successor | VDA 231-106 classification | |
|---|---|---|---|---|---|---|---|---|---|
| CW453K (DIN EN 12163 : 2011-08) | CW453K | DIN EN 12163 : 2011-08 | DIN EN 12163 : 2011-08 replaced by DIN EN 12163 : 2016-11 | Replaced | Germany | CuSn8 | CuSn8 | 3.2 | 1) |
| 1) Remark: CuSn8, mat. No. CW453K, is comparable to the DIN-make CuSn8, mat. No. 2.1030, acc. to DIN 17662 : 1983-12. Properties of the CuSn-alloy are predominantly determined by the tin-content. Tensile strength, yield point and hardness increase according to the rising cold forming grade, elongation after fracture decreases. Electrical and thermal conductivity are lower than for pure copper. Very high resistance to corrosion, particularly to atmospheric influences, seawater, sulfite liquor, carbonated and salted mine water. The alloys are stress corrosion-proof. Processing properties: warm forming: medium cold forming: very good machinability: medium hard soldering: good soft soldering: good gas shielded welding: good burnishing: good Application: For friction elements, especially for thin-walled friction-bearing bushings and sliding strips as well as for beater bars. Increased abrasion and corrosion resistance compared to CuSn6. For the electrolytically tinned strip the coatings (Sn bright, Sn matt, Sn fuzed, SnPb) are listed by the application (better solderability, better corrosion resistance, reduction of the electrical contact resistance, better appearance) in the DIN EN 14436 : 2004-11 (Table 5) |
Chemical Composition
| Fe [%] | Ni [%] | P [%] | Pb [%] | Sn [%] | Zn [%] | |
|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||||
| 2) Remark: blur |
Mechanical Properties
| Semi-finished Product | Condition | Strength Abbrevation | Nominal Size [mm] | Temperature [°C] | Tensile Strength [MPa] | Yield Strength (0.2% offset) [MPa] | Elongation A100 [%] | Elongation A11,3 [%] | Elongation A [%] | Hardness HB | HBW | |
|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1)2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| 1) Source: blur | |||||||||||
| 2) Remark: blur | |||||||||||
| 3) Source: blur |
Physical Properties
| Condition | Temperature [°C] | Melting Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Poisson's Ratio | Mean Coefficient of Thermal Expansion [10^-6*K^-1] | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | Electric Conductivity [MS/m] | Specific Electric Conductivity [% IACS] | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| 1) Source: blur | |||||||||||||
| 2) Source: blur | |||||||||||||
| 3) Source: blur |
Heat Treatment
| Heat Treatment | Temperature [°C] | |
|---|---|---|
| blur | blur | 1)2) |
| blur | blur | 1)2) |
| blur | blur | 1)2) |
| 1) Source: blur | ||
| 2) Remark: blur |
Cross Reference
| Material Name | Country | Standard | |
|---|---|---|---|
| CuSn8 | Europe | EN 12163 | |
| BrOF7-0,2 | Russia | GOST 5017 | 1) |
| CuSn8 | International | ISO 427 | 1) |
| C52100 | USA | UNS | 1) |
| B103 UNS C52100 | USA | ASTM B103 | 1) |
| B139 UNS C52100 | USA | ASTM B139 | 1) |
| SnBz8 | Germany | 1) | |
| CuSn8 | Germany | DIN 17662 | 2) |
| 2.1030 | Germany | DIN 17662 | 2) |
| 1) Source: Deutsches Kupferinstitut Berufsverband e.V., Düsseldorf | |||
| 2) Source: DIN CEN/TS 13388 (DIN SPEC 9700) |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| 283 | William Prym Holding GmbH, Stolberg |
| 4030 | VDM Metals GmbH, Frankfurt/Main |
| B09 | Wieland-Werke AG, Ulm |
| B10 | Wieland-Werke AG, Ulm |
| B18 | Wieland-Werke AG, Ulm |
| BB80 | Sundwiger Messingwerk GmbH & Co.KG, Hemer |
| BD80 | Sundwiger Messingwerk GmbH & Co.KG, Hemer |
| Caroba | Wieland Metal Services Germany GmbH, Düsseldorf |
| Carobronze | Wieland Metal Services Germany GmbH, Düsseldorf |
| CuSn8 | Heraeus Deutschland GmbH & Co. KG, Hanau |
| CuSn8 | Mittelrheinische Metallgießerei H. Beyer GmbH & Co KG, Andernach |
| CuSn8 | CSN Carl Schreiber GmbH, Neunkirchen |
| CuSn8 | Wieland-Werke AG, Velbert |
| CuSn8 | KME Germany GmbH, Osnabrück |
| CuSn8 | Nussbaum Metallhandel GmbH, Bad Wörishofen |
| CuSn8 | MPG Mendener Präzisionsrohr GmbH, Menden |
| CuSn8 | Feindrahtwerk Adolf Edelhoff GmbH & Co, Iserlohn |
| CuSn8 | Schreier Metall GmbH, Erkrath |
| CuSn8 | G.Rau GmbH & Co. KG, Pforzheim |
| CuSn8 | Gebr. Kemper GmbH + Co, Olpe/Biggesee |
| CuSn8 | Wieland Metal Services Germany GmbH, Düsseldorf |
| CuSn8 | Vossloh Aktiengesellschaft, Werdohl |
| CuSn8 | Eugen Geyer GmbH, Königsbach-Stein |
| CuSn8 | J.G. Dahmen & Co. GmbH & Co. KG, Iserlohn |
| CuSn8 | Manfred J.C. Niemann, Bremen |
| Nida | VDM Metals GmbH, Frankfurt/Main |
| PAN-WBz8 | PAN-Metallgesellschaft, Mannheim |
| Pro-8 | Wieland Metal Services Germany GmbH, Düsseldorf |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
| blur | blur |
Coefficient thermal expansion
| Related Temperature [°C] | Temperature [°C] | Coefficient thermal expansion [10^-6*K^-1] |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
Yield strength
| Temperature [°C] | 0.1% Proof strength [MPa] | 0.2% Proof strength [MPa] | Yield strength [MPa] |
|---|---|---|---|
| blur | blur | blur | blur |
| blur | blur | blur | blur |
| blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |