Cu-ETP | CW004A Material Datasheet
Unlock Exclusive Materials Data
Gain access to a wealth of materials data by joining our Materials Portal.
Register for Free or Upgrade for Full AccessMaterial Description
| Material Number | Material Number (single) | Standard | Range of Application | Standard Status | Country | |
|---|---|---|---|---|---|---|
| CW004A (DIN EN 1977 : 2013-04) | CW004A | DIN EN 1977 : 2013-04 | Supersedes DIN EN 1977 : 1998-05 | Valid | Germany | 1) |
| 1) Remark: The drawing stock (circular cross-section, from Ø 6 mm) is used for fabrication into wire by cold drawing, principally for the manufacture of electrical conductors, also for use on overhead contact lines. |
Chemical Composition
| Bi [%] | Cu [%] | O [%] | Pb [%] | |
|---|---|---|---|---|
| blur | blur | blur | blur | 1)2) |
| 1) Source: blur | ||||
| 2) Remark: blur |
Mechanical Properties
| Semi-finished Product | Condition | Area [mm²] | Tensile Strength [MPa] | Elongation A100 [%] | |
|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | 1) |
| 1) Source: blur |
Physical Properties
| Condition | Temperature [°C] | Melting Temperature [°C] | Density [g/cm³] | Young's Modulus [GPa] | Poisson's Ratio | Mean Coefficient of Thermal Expansion [10^-6*K^-1] | Mean Coefficient of Thermal Expansion (reference 20°C) [10^-6*K^-1] | Thermal Conductivity [W/(m*K)] | Specific Electrical Resistance [µΩm] | Mean Specific Heat Capacity [kJ/(kg*K)] | Electric Conductivity [MS/m] | Specific Mass Resistance [Ωg/m²] | Specific Electric Conductivity [% IACS] | |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 1) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 2) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 3) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4) |
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | blur | 4) |
| 1) Source: blur | ||||||||||||||
| 2) Source: blur | ||||||||||||||
| 3) Source: blur | ||||||||||||||
| 4) Source: blur |
Cross Reference
| Material Name | Country | Standard | |
|---|---|---|---|
| 110 | Australia | AS 2737 | 1) |
| ETP | Australia | AS 2737 | 1) |
| T2 | China | GB/T 5231 | 1) |
| Cu-ETP | Germany | EN 50149 | |
| Cu-ETP | Europe | EN 1977 | |
| Cu-ETP | Europe | EN 50149 | |
| Cu-ETP | International | ISO 4738 | 1) |
| C1100 | Japan | JIS H 3260 | 1) |
| M0 | Russia | GOST 859 | 1) |
| B49 UNS C11000 | USA | ASTM B49 | 1) |
| C11000 | USA | UNS | 1) |
| E-Cu58 | Germany | DIN 1787 | 2) |
| 2.0065 | Germany | DIN 1787 | 2) |
| 1) Source: Deutsches Kupferinstitut Berufsverband e.V., Düsseldorf | |||
| 2) Source: DIN CEN/TS 13388 (DIN SPEC 9700) |
Producer/Supplier/Trade names
| Tradename | Supplier |
|---|---|
| CW004A | OTTO BRENSCHEIDT GmbH & Co. KG, Sundern |
| CW004A | KME Mansfeld GmbH, Hettstedt |
| CW004A | Sundwiger Messingwerk GmbH & Co.KG, Hemer |
Material Compliance
| REACh | RoHS |
|---|---|
| blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
Coefficient thermal expansion
| Related Temperature [°C] | Temperature [°C] | Coefficient thermal expansion [10^-6*K^-1] |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Specific heat
| Temperature [°C] | Specific heat [kJ/(kg*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Density
| Temperature [°C] | Density [g/cm³] |
|---|---|
| blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Thermal conductivity
| Temperature [°C] | Thermal conductivity [W/(m*K)] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Designation
| Designation | Material number | Source |
|---|---|---|
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
| blur | blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
| blur | blur | blur | blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Linear-elastic
| Temperature [°C] | Young's modulus [GPa] | Bulk modulus [GPa] | Shear modulus [GPa] | Poisson's ratio |
|---|---|---|---|---|
| blur | blur | blur | blur | blur |
Electrical resistivity
| Temperature [°C] | Specific electrical resistance [µΩm] |
|---|---|
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Strain life
| Temperature [°C] | Static hardening coefficient [MPa] | Static hardening exponent | Cyclic fatigue strength coefficient [MPa] | Cyclic fatigue strength exponent | Ductility coefficient [Pa] | Ductility exponent | Cyclic strength coefficient [MPa] | Cyclic strain hardening exponent | Young's modulus [GPa] |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |
Tensile strength
| Temperature [°C] | Tensile strength [MPa] |
|---|---|
| blur | blur |
Classification
| WIAM Material | Treatment | Semi-finished product | Dimension [mm] | Load type | Failure criteria | Rolling direction | Maximum stress [MPa] | Strain at maximum stress [%] | Source description |
|---|---|---|---|---|---|---|---|---|---|
| blur | blur | blur | blur | blur | blur | blur | blur | blur | blur |